Abstract:The most of commercial isotactic polypropylene (PP) polymers exhibit low melt strength due to lack of a long-chain-branched (LCB) structure, which significantly limits PP processing operations. There are several chemical methods available today to prepare high-melt-strength PP (HMS-PP) products containing a small amount of LCB structures. However, the processes require multiple reaction steps, forming a complicated mixture of branch structures (i.e., branch length, branch density, and impurity, etc.). This work discusses an efficient and economic method following a commercial PP production process (i.e., polymerization and then extrusion). The direct-polymerization step is centered on an asymmetric diene co-monomer p-(3-butenyl)styrene (BSt) that can be randomly incorporated in the PP chain with a mono-enchainment fashion by the fourth generation MgCl2-supported TiCl4 catalyst in the slurry polymerization process. The predominate coordination/1,2-insertion of the α-olefin moiety in the BSt co-monomer forms linear PP-co-BSt copolymer (granules), with few pendant styrene moieties randomly distributed along the polymer chain. Following the common PP extruding and pelletizing procedure at 200 °C, the molten PP-co-BSt copolymer engages the in situ coupling reaction between pendant styrene units in neighboring polymer chains to spontaneously form PP branches with long branch lengths. The branch densities in the resulting LCB-PP pellets are controlled by the BSt content in the copolymer and the degree of the thermally induced coupling reaction. The resulting LCB-PP polymer, with an average of one to four LCB structures per chain, is completely melt-processable, exhibiting high melt strength under elongation flows. The same strain-hardening phenomenon was also observed in the polymer blends between these LCB-PP polymers and linear PP homopolymer with the composition up to 1/1 weight ratio.

Fabrication of Long Chain Branched Polypropylene Using Click Chemistry

A Comprehensive Review on Controlled Synthesis of Long-Chain-Branched Polyolefins: Part 2, Multiple Catalyst Systems and Prepolymer Modification

A Convenient, Highly-Efficient Method for Preparation of Hydroxyl-Terminated Isotactic Poly（propylene） and Functional Di-Block Copolymer

Facile functionalization of isotactic polypropylene by azide and alkyne groups for click chemistry application

Synthesis of Azide End‐functionalized Isotactic Polypropylene Building Block and Renewed Modular Synthesis of Diblock Copolymers of Isotactic Polypropylene and Poly(ε‐caprolactone)

Preparation of high melt strength polypropylene by the reactive extrusion process and its foaming application

Synthesis of Long-Subchain Hyperbranched Polypropylene Using Thermally Degraded Products as Precursor

A novel strategy for the preparation of long chain branching polypropylene and the investigation on foamability and rheology

The preparation and rheology characterization of long chain branching polypropylene

Impact Polypropylene Copolymers Containing Multifold H-shape Long-Chain-branching Structures: Synthesis and Properties

Preparation of Well-Controlled Isotactic Polypropylene-Based Block Copolymers with Superior Physical Performance via Efficient Coordinative Chain Transfer Polymerization

Preparation and Characterization of High Melt Strength Polypropylene with Long Chain Branched Structure by the Reactive Extrusion Process

Influence of Molecular Structure on the Rheological Properties and Foamability of Long Chain Branched Polypropylene by “One-Pot” Reactive Extrusion

Nonconjugated α,ω-Diolefin/Propylene Copolymerization to Long Chain-Branched Polypropylene by Ziegler–Natta Catalyst: Overcoming Steric Hindrance by Introducing an Extra Electronic Pulling Effect

Direct Synthesis of High-Melt-Strength Polypropylene Using the Fourth Generation Heterogeneous Ziegler–Natta Catalyst and Commercial Production Process

Facile Synthesis of Functional Poly( Ε -Caprolactone) Via Janus Polymerization

Preparation of Long Chain Branched Pp Via Multi-Monomer Melt Grafting in the Presence of Bi-Functional Monomer 1,6-Hexanediol Diacrylate

Conformation transition and crystalline phase variation of long chain branched isotactic polypropylenes (LCB-iPP)

SYNTHESIS OF STYRYL-CAPPED POLYPROPYLENE Via METALLOCENE- MEDIATED COORDINATION POLYMERIZATION： APPLY TO POLYPROPYLENE MACROMOLECULAR ENGINEERING

Rheology and thermal behavior of long branching polypropylene prepared by reactive extrusion

New effort to synthesize star isotactic polypropylene