Abstract:The most of commercial isotactic polypropylene (PP) polymers exhibit low melt strength due to lack of a long-chain-branched (LCB) structure, which significantly limits PP processing operations. There are several chemical methods available today to prepare high-melt-strength PP (HMS-PP) products containing a small amount of LCB structures. However, the processes require multiple reaction steps, forming a complicated mixture of branch structures (i.e., branch length, branch density, and impurity, etc.). This work discusses an efficient and economic method following a commercial PP production process (i.e., polymerization and then extrusion). The direct-polymerization step is centered on an asymmetric diene co-monomer p-(3-butenyl)styrene (BSt) that can be randomly incorporated in the PP chain with a mono-enchainment fashion by the fourth generation MgCl2-supported TiCl4 catalyst in the slurry polymerization process. The predominate coordination/1,2-insertion of the α-olefin moiety in the BSt co-monomer forms linear PP-co-BSt copolymer (granules), with few pendant styrene moieties randomly distributed along the polymer chain. Following the common PP extruding and pelletizing procedure at 200 °C, the molten PP-co-BSt copolymer engages the in situ coupling reaction between pendant styrene units in neighboring polymer chains to spontaneously form PP branches with long branch lengths. The branch densities in the resulting LCB-PP pellets are controlled by the BSt content in the copolymer and the degree of the thermally induced coupling reaction. The resulting LCB-PP polymer, with an average of one to four LCB structures per chain, is completely melt-processable, exhibiting high melt strength under elongation flows. The same strain-hardening phenomenon was also observed in the polymer blends between these LCB-PP polymers and linear PP homopolymer with the composition up to 1/1 weight ratio.

Synthesis of Long-Subchain Hyperbranched Polypropylene Using Thermally Degraded Products as Precursor

Synthesis and Thermomechanical and Rheological Properties of Biodegradable Long-Chain Branched Poly(Butylene Succinate-Co-Butylene Terephthalate) Copolyesters

A Convenient, Highly-Efficient Method for Preparation of Hydroxyl-Terminated Isotactic Poly（propylene） and Functional Di-Block Copolymer

Preparation of high melt strength polypropylene by the reactive extrusion process and its foaming application

The preparation and rheology characterization of long chain branching polypropylene

Rheology and thermal behavior of long branching polypropylene prepared by reactive extrusion

Preparation and Characterization of High Melt Strength Polypropylene with Long Chain Branched Structure by the Reactive Extrusion Process

Synthesis and Characterization of High‐density Polypropylene‐grafted Polyethylene Via a Macromolecular Reaction and Its Rheological Behavior

A novel strategy for the preparation of long chain branching polypropylene and the investigation on foamability and rheology

Preparation of Long Chain Branched Pp Via Multi-Monomer Melt Grafting in the Presence of Bi-Functional Monomer 1,6-Hexanediol Diacrylate

Fabrication of Long Chain Branched Polypropylene Using Click Chemistry

Direct Synthesis of High-Melt-Strength Polypropylene Using the Fourth Generation Heterogeneous Ziegler–Natta Catalyst and Commercial Production Process

Rheology and Thermal Properties of Long Chain Branching Polypropylene by Reactive Extrusion

Rheology and Melt Strength of Long Chain Branching Polypropylene Prepared by Reactive Extrusion with Various Peroxides

Influence of Polyfunctional Monomer on Melt Strength and Rheology of Long‐chain Branched Polypropylene by Reactive Extrusion

The melt grafting preparation and rheological characterization of long chain branching polypropylene

Influence of Molecular Structure on the Rheological Properties and Foamability of Long Chain Branched Polypropylene by “One-Pot” Reactive Extrusion

Rheology and Thermal Properties of Polypropylene Modified by Reactive Extrusion with Dicumyl Peroxide and Trimethylol Propane Triacrylate

Enhancing Mechanical Performance of High-Lignin-Filled Polypropylene via Reactive Extrusion

High Melt Performance Poly (lactic acid) with Dual Hybrid Long Branching Chains Prepared by Chain Degradation and Restructuring

Architecting Branch Structure in Terpolymer of CO 2 , Propylene Oxide and Phthalic Anhydride: an Enhancement in Thermal and Mechanical Performances