Preparation of Highly Branched Polyolefins by Controlled Chain‐walking Olefin Polymerization
Tong Lei,Zhanshan Ma,Hongju Liu,Xiaoyue Wang,Pei Li,Feifei Wang,Weitai Wu,Shaojie Zhang,Guoyong Xu,Fuzhou Wang
DOI: https://doi.org/10.1002/aoc.6788
IF: 3.9
2022-01-01
Applied Organometallic Chemistry
Abstract:A series of alpha-diimine nickel(II) catalysts bearing different para-substituted groups, {[(4-R-2,6-Me-2-C6H2N(sic)C)(2)Nap]NiBr2, Nap: 1,8-naphthdiyl; R = CHMePh (C1); R = CHPh2 (C2); R = Bu-t (C3); R = Br (C4); R = Me (C5)}, were synthesized and characterized. The molecular structures of C1 and C3 were determined by single crystal X-ray analysis and show distorted tetrahedron geometry with C-2v symmetry. The catalytic behaviors of these catalysts toward ethylene polymerization were investigated in the presence of diethylaluminum chloride (Et2AlCl) as a cocatalyst. The fast chain-walking process in N,N-chelated nickel system can be efficiently modulated via the introduction of para-sec-phenethyl substituents with improved thermal stability and catalytic performance. C1-Et2AlCl exhibited high thermal stabilities and high activities reaching 4.61 x 10(6) g PE (mol Ni h)(-1), producing highly branched amorphous polyethylenes (up to 143 branches/1000C) with high molecular weight and narrow polydispersity. This catalyst system conducted successfully conducted 2-octene polymerization in comparison with the corresponding 1-octene polymerization. The result demonstrated 2-octene polymerized slower than 1-octene and produced the highly-branched poly(2-octene)s with approximately 120 branches/1000C, including methyl, ethyl, amyl, and hexyl branches and a small amount of the long methylene sequence due to monomer isomerization.