Abstract:Titania nanotubes (TNTs) were synthesized by hydrothermal treatment of rutile-phase TiO2 nanoparticals in NaOH solution at 110 degrees C for 24 hours. After drying in aceton for 36 h, the TNTs were under vacuum drying for 24 h at room temperature. The Pt-inserted titania nanotubes (Pt/TNTs) were obtained by filling H2 PtCl6 ethanol solution into the TNTs after vacuum drying. The characterizations of the as-synthesized samples were confirmed by TEM, XRD, and UV-Vis. The photocatalytic activity of the Pt/TNTs was investigated by photo-induced decomposition of methyl orange(MO)under the main 365 nm UV-light. In order to comparison, the photocatalytic activity of both the rutile-phase TiO2 nanoparticles and pure TNTs were also investigated at the same time under the same experimental conditions. The TEM images show that the TNTs are hollow, a few hundred nanometers long, and the inner/outer diameter is about 6/10 nm. The crystal structure of TNTs is H2Ti2O5 x H2O with a little Na. Both the shape and the crystalline of the TNTs are not changed after the modification. The oval or round Pt0 nanoparticals, about 3 nm in diameter, are found only in the nanotubes. Pt/TNTs exhibit enhanced absorption at the visible range in the UV-Vis spectra and its start absorption band edge(lambda0 approximately 457 nm)is obviously redshifted compared to the rutile-phase TiO2 nanoparticals and pure TNTs. The Pt nanoparticles are found to significantly enhance the photocatalytic activity of TNTs. Pt/TNTs are demonstrated to be highly efficient for the UV-light induced photocatalytic decomposition of MO compared to both the rutile-phase TiO2 nanoparticals and pure TNTs. After irradiation for 60 min, the photocatalysis decomposition rate of MO in rutile-phase TiO2 nanoparticals, TNTs and Pt/TNTs are 46.8%, 57.2% and 84.6% respectively.

Fabrication and Characterization of Titanium Based Nanotubes

Fabrication of Well-Aligned Tio2 Nanotube Arrays with Outstanding Light-Induced Hydrophilicity Performance

Preparation and Characterization of Titanate Nanotubes by Hydrothermal Method

Preparation and characterization of titanium oxide nanotubes

Synthesis and characterization of high-aspect-ratio titania nanotubes

Synthesis and characterization of anatase TiO2 nanotubes with uniform diameter from titanium powder

Characterization, Properties and Catalytic Application of TiO2 Nanotubes Prepared by Ultrasonic-Assisted Sol-Hydrothermal Method

Fabrication and Photocatalytic Activity of Pt-Inserted Titania Nanotubes

The Fabrication and Characterization of Novel Carbon Doped TiO2nanotubes, Nanowires and Nanorods with High Visible Light Photocatalytic Activity

Preparation and Characterization of TiO2 Nanotube Arrays on Porous Titanium

Fabrication of Self-Organized Tio2 Nanotubes by Anodization and Its Photocatalytic Properties

Facile microwave-assisted hydrothermal synthesis of TiO2 nanotubes

Fabrication of rutile TiO2 tapered nanotubes with rectangular cross-sections via anisotropic corrosion route.

A Novel Fabrication of Silver-Modified 3D Singlecrystal Nanowires-Assembled Rutile TiO 2 Nanoflowers with Enhanced Visible Photocatalytic Activities

Simple Fabrication of Thermally Stable Apertured N-doped TiO2 Microtubes As a Highly Efficient Photocatalyst under Visible Light Irradiation

Titanium oxide nanotubes, nanofibers and nanowires

Preparation of High-Orderly Tio2 Nanotubes in Organic Solution and Characterization of C-Doped Tio2

Fabrication And Fluorescence Property Of Titanium Dioxide Nanotube Arrays By Anodizing Processes

Preparation and Structure Analysis of Titanium Oxide Nanotubes

Synthesis of titanate nanotubes and the mechanism of their formation

Synthesis of Titanium Dioxide Nanotubes with Different N-Containing Ligands via Hydrothermal Method