Preparation of Resorcinol Diglycidyl Ether and Its Application

YUAN Hui-wu,RAO Qiu-hua

DOI: https://doi.org/10.3969/j.issn.1002-7432.2007.05.001

2007-01-01

Abstract:Resorcinol diglycidyl ether(RDGE) which epoxide number was 0.80 and viscosity was 0.36 Pa·s at 25 ℃ was obtained from resorcin and epichlorhydrine(ECH) by using triphenyl phosphine as ethrification catalyzer and NaOH as cyclolization catalyzer.The curing exothermic peak at DSC curve was lower 15 ℃ than conventional bisphenol A epoxy resin(E51),the viscosity of E51 could be decreased obviously and the comprehensive properties of epoxy resin was tremendously enhanced by blending it with RDGE.When blending was cured with 593#,the tensile strength of RDGE and E51 cured were 75.17MPa and 58.5 MPa separately and that of the former was increased 28% more than that of latter,the tensile strength,flexural strength and modulus of cured blending of RDGE and E51 were linearly increased with increasing RDGE content,the flexural strength of RDGE and E51 cured were 123.75 MPa and 112.77 MPa separately and there flexural modulus were 2.40 GPa and 1.79 GPa.When blending was cured with polyamide 651,the tensile strength was most,such as 53 MPa at which RDGE content was 80%.