Optical, vibrational, and photoluminescence properties of holmium‐doped boro‐bismuth‐germanate glasses
Mamilla Rathaiah,Rallapalli Ravanamma,Nirlakalla Ravi,Kummara Venkata Krishnaiah,Kagola Upendra Kumar,Nallabala Nanda Kumar Reddy,Bangaram Naga Kiran,Chinnappa
DOI: https://doi.org/10.1002/bio.4822
IF: 2.613
2024-07-19
Luminescence
Abstract:The optical, vibrational, and photoluminescence properties of Ho3+‐doped boro‐bismuth‐germanate glasses were studied. Upon 450 nm excitation, intense green emission around 550 nm was observed in low Ho3+‐doped glasses, whereas high Ho3+ doping leads to the concentration quenching effect; the reasons behind the quenching of emission intensity and decay time of 5S2 + 5F4 (Ho3+) level have been discussed. The studied glasses could be a good choice for display devices and green emission applications. Holmium (Ho3+)‐doped boro‐bismuth‐germanate glasses having the chemical composition (30‐x)B2O3 + 20GeO2 + 20Bi2O3 + 20Na2O + 10Y2O3 + xHo2O3, where x = 0.1, 0.5, 1.0, and 2.0 mol% were prepared by melt‐quenching technique. The prepared glasses were examined for thermal, optical, vibrational, and photoluminescent properties. The prepared glasses were found to be thermally very stable. The optical bandgap and Urbach energies of 0.1 mol% Ho2O3‐doped boro‐bismuth‐germanate glass were calculated to be 3.3 eV and 377 MeV, respectively, using the absorption spectrum. The Judd–Ofelt analysis was performed on the 0.1 mol% Ho2O3‐doped glass and compared the obtained parameters with literature. The branching ratio (β) and emission cross‐section (σem) of the green band were determined to be 0.7 and 0.24 × 10−20 cm2, respectively. Under 450 nm excitation, a strong green emission around 550 nm was observed and assigned to the (5S2 + 5F4) → 5I8 (Ho3+) transition. Upon an increase of Ho2O3 content from 0.1 to 2.0 mol%, the intensities of all observed emission bands as well as decay time of the (5S2 + 5F4) → 5I8 transition have been decreased gradually. The reasons behind the decrease in emission intensity and decay time were discussed. The strong green emission suggests that these glasses may be a better option for display devices and green emission applications.
chemistry, analytical