Sensitized Up-Conversion Luminescence of Ho 3+ in Nd 3+ -Yb 3+ -Ho 3+ Co-Doped ZrF 4 -Based Glass

Shaukat S. F.,Dong Ya-Ming,Hussain M.,Farooq R.,Li Guang-Yuan

DOI: https://doi.org/10.1007/s11741-002-0005-4

2002-01-01

Abstract:Up-conversion processes for the blue, green and red emissions were found two-photon phenomenon, known as the cooperative phenomenon. This phenomenon was assisted by Nd 3+ → Yb 3+ → Ho 3+ energy transfer. The strong green emission due to the Ho 3+ : ( 5 F 4 , 5 S 2 )→ 5 I 8 transitions was observed in Nd 3+ -Ho 3+ co-doped ZrF 4 -based fluoride glasses under 800 nm excitation. As an attempt to enhance Ho 3+ up-conversion luminescences in the Nd 3+ – Ho 3+ co-doped ZrF 4 -based glasses, Yb 3+ ions were added to the glasses. As a result it was found that, in 800 nm excitation of 60 ZrF 4 . 30BaF2. (8- x )LaF 3 . lNdF 3 . x YbF 3 . 1HoF 3 glasses ( x =0 to 7), sensitized up-conversion luminescences are observed at around 490 nm (blue), 545 nm (green), and 650 nm (red), which correspond to the Ho 3+ : 5 F 3 → 5 I 8 , ( 5 F 4 , 5 S 2 )→ 5 I 8 and 5 F 5 → 5 I 8 transitions respectively. The intensities of the green and red emissions in a 3 mol % YbF 3 -containing glass were about 50 times stronger than those glasses without YbF 3 . This is based on sensitization due to Yb 3+ ions. In particular, the green emission was extremely strong and the Nd 3+ -Yb 3+ -Ho 3+ co-doped ZrF 4 -based glasses have a high possibility of realizing a green up-conversion laser glass. In this paper the up-conversion mechanism in the glasses is discussed in detail.