Abstract:Aim. It is well known that Fe-Co-Si alloys are excellent soft magnetic materials. However, their rapid solidification mechanisms and rapid dendritic growth mechanisms are not clear. We now present our preliminary results of exploration on the two mechanisms for Fe-32.29%Co-20.33%Si ternary alloy, which is undercooled up to 378 K (0.25TL). In the full paper, we explain our exploration results in some detail; in this abstract, we just add some pertinent remarks to listing the two topics of explanation. The first topic is: the experimental method. In this topic, we use the glass fluxing method to realize rapid solidification and use differential scanning calorimeter (DSC), X-ray diffraction (XRD) meter and scanning electronic microscope (SEM) to characterize the samples of the alloy. The second topic is: the experimental results and their analysis. Its first subtopic is: DSC thermal analysis and phase constitution. The DSC analysis shows that the solidus and liquidus temperatures of the alloy are 1148 K and 1535 K respectively. The solidified microstructure consists of α(Co, Fe)2Si and (Fe, Co)5Si3 phases within the undercooling range of 98-378 K. When the alloy melt begins to solidify, metastable supersaturated β(Co, Fe)2Si solid solution phase forms first. During the subsequent precipitation transition, (Fe, Co)5Si3 phase appears and metastable β(Co, Fe)2Si phase transforms into stable α(Co, Fe)2Si phase. The second subtopic of the second topic is: solidification microstructures under nonequilibrium condition. The typical solidification microstructures at various undercoolings are presented in Fig.3. (Fe, Co)5Si3 phase generates mainly inner α(Co, Fe)2Si grains, while a few (Fe, Co)5Si3 grains nucleate on α(Co, Fe)2Si grain boundaries. The third subtopic of the second topic is: dendritic growth mechanism of (Co, Fe)2Si. The measured β(Co, Fe)2Si dendritic growth velocities in Fe-32.29%Co-20.33%Si are shown in Fig.4(a). As undercooling increases, the dendritic growth velocity of β(Co, Fe)2Si phase increases according to the exponential relation: V=0.04e0.01ΔT.

Competitive Nucleation and Rapid Growth of Co-Si Intermetallic Compounds During Eutectic Solidification under Containerless Processing Condition

Containerless rapid solidification of highly undercooled Co-Si eutectic alloys

Exploring growth characteristics of intermetallic compound in ternary Fe-Co-Si alloy

Nucleation and growth of βCu3Sb intermetallic compound in undercooled Cu–31% Sb eutectic alloy

Rapid Eutectic Growth under Containerless Condition

Phase separation and morphology formation of Co-Cu-Si ternary alloy

Metastable Solidification of Hypereutectic Co2Si-CoSi Composition: Microstructural Studies and In-Situ Observations

Microstructure Evolution and Solidification Kinetics of Undercooled Co–Ge Eutectic Alloys

Ternary eutectic and peritectic solidification of undercooled liquid Fe–Mo–Si alloys

Rapid Solidification of Non-Stoichiometric Intermetallic Compounds: Modeling and Experimental Verification

Containerless Rapid Solidification of Undercooled Cu-Co Peritectic Alloys

Thermodynamic Properties and Phase Transitions of Ternary Co–Cu–Si Alloys with Equiatomic Co/Cu Ratio

Rapid Growth Kinetics and Microstructure Modulation of Intermetallic Compounds Within Containerlessly Solidifying Mo-Co Refractory Alloys

Macroscopic Phase Separation and Primary FeSi Compound Growth Within Undercooled Ternary Fe–Sn–Si Monotectic Alloy

Rapid Solidification of Undercooled Al-Cu-Si Eutectic Alloys

Metastable Solidification Pathways of Undercooled Eutectic CoSi–CoSi2 Alloys

Solute Distribution Within Rapidly Grown Fe-Co Single Phase

Thermal Expansion and Thermal Diffusivity Properties of Co-Si Solid Solutions and Intermetallic Compounds

Microstructural characterization of cobalt–antimony eutectic alloy droplets solidified in drop tube

Solidification behaviour of undercooled Co–Cu alloys showing a metastable miscibility gap

Metastable Phase Separation And Rapid Solidification Of Undercooled Co40fe40cu20 Alloy