Abstract:For further knowledge about the refining performance of AlTiC master alloys, A15.5Ti0.25C and A16.5Ti0.5C master alloys containing high Ti and C content were prepared and used in grain refining experiments of 99.8% commercial pure aluminum(CPAl). Their performance was compared with two types of Al5Ti1B refiners whose performance was nowadays considered to be the best. These two types of master alloys show similar refining efficiency at the addition level of 0.2%. However, at the addition level of 0.5%, there still exists great performance difference between AlTiC and Al5TiB alloys in grain refinement of 99.98% and 99.995% high purity aluminum(HPAl). The growth of columnar grains is fully suppressed due to the refinement of AlTiC at the addition level of 0.5%. Also, at the same addition level, the grain refining experiments of A13Ti0.15C and A15Ti0.2C master alloys which have found initial commercial applications are conducted in the above-mentioned three types of pure aluminum. According to the experimental results, these two refiners of different compositions are both nonideal. The second phase particles extracted from each refiner were observed through TEM, while the nuclei of grains after grain refinement were observed through SEM. The results were analyzed through computation and comparison of the constitutional-supercooling parameter and the growth-restriction parameter whose values were determined by solute element in aluminum melt with different purity. Apparently, AlTiC master alloys with high content of Ti and C element have great refining potential.

Grain Refining Mechanisms of Casting Aluminum Alloy

Development of Mechanism of Grain Refinement in Aluminum

On the Understanding of Aluminum Grain Refinement by Al-Ti-B Type Master Alloys

Grain Refinement of Al–Si–Cu Alloys by AlB2 and (Al,Ti)B2

Research Progress of Al-Ti-B Grain Refiner

Quantities of grains of aluminum and those of TiB2 and Al3Ti particles added in the grain-refining processes

The Evaluating Study of the Refining Effect of Al-Ti-C and Al-Ti-B on Aluminum

Grain Refinement of Al-5Ti-0.62C-0.2Nd Grain Refiner for Commercial Pure Aluminum and Its Effect on Mechanical Properties

Research of Grain Refining on Pure Al by Three Different Master Alloys

STUDY ON THE MICROSTRUCTURES AND GRAIN REFINING PERFORMANCE OF Al-Ti-C GRAIN REFINING MASTER ALLOYS

Study on Grain Refining and Metamorphism of ZL111 Aluminium Alloys

Study on Grain Refinement and Refining Mechanism of Al-Si-Mg Alloy

An experimental study of the effect of Ag, Cu, Li, Mg, Ni, Ti, Sc, Zr on grain refining in binary and multicomponent Al-based alloys

Development of Grain Refinement in Aluminium Field

The grain refinement of high-purity aluminum by aluminum-transition metal alloys

Development Process and Future Trends of Chemical Refining Agents' Influence on Grain Refinement in Aluminum Alloys

The Grain Refinement Mechanism of AlTiC, Al4B and Al3Ti4B Master Alloy in Pure Aluminium and Hypoeutectic Al-Si Alloys

Achieving superior grain refinement efficiency for Al–Si casting alloys through a novel Al–La–B grain refiner

Performance Comparison of AlTiC and AlTiB Master Alloys in Grain Refinement of Commercial and High Purity Aluminum

Effect of Fe and Si on Grain Refinement of Commercial Purity Aluminum

The Grain Refinement of 1070 Alloy by Different Al-Ti-B Mater Alloys and Its Influence on the Electrical Conductivity