Stabilization of MSWI Fly Ash by Glass-ceramics Recycling Process

YANG Jia-kuan,XIAO Ming-dan,ZHOU Min,HE Bao-ping,ZHANG Du-du,XIAO Bo
DOI: https://doi.org/10.3969/j.issn.1000-2871.2007.03.001
2007-01-01
Abstract:Municipal solid waste incineration(MSWI) fly ash is classified as hazardous solid waste because of a lot of heavy metals and dioxins in it.Fly ash samples were taken from an incineration power plant in Guangdong province,which is the first solid waste power plant with the rotary kiln process developed by themselves in China.Based upon analyses of chemical and mineral compositions of fly ash samples,the matrix glasses and glass-ceramics have been made from fly ash with some additives.The crystallization of the matrix glasses,crystalline phase and microstructural characteristics of glass-ceramics have been investigated by DSC,XRD and SEM.The leachate properties of fly ash samples,solidified body by cement and solidified body by molten glass have been studied respectively.The results show that the chemical compositions of MSWI fly ash are comprised of SiO2,CaO,Al2O3,Fe2O3 and MgO,all of which are also the necessary chemical components for glass.Due to the above mentioned facts the glass and glass-ceramics can be made from fly ash successfully.The transition temperature Tg of matrix glass is about 700 ℃.The different glass-ceramic samples are treated at the fixed nucleation temperature 700℃ for 2h followed by heat-treatment at various crystallization temperatures.With the increase of crystallization temperatures,a part of crystals grow into column crystals larger than 300~400nm,and microstructure of glass-ceramics becomes sparse.The major crystalline phase was diopside.The leaching value of Cd in MSWI fly ash is higher than the national standard.The leaching values of heavy metals of solidified body by cement and molten glass are far lower than that of the national standard in China,and the leaching value of heavy metals of solidified body by glass is one order of magnitude lower than that of solidified body by cement.
What problem does this paper attempt to address?