Characterization and Leaching Behavior of Fly Ashes from Power Plants in Yanzhou Mining District
GJ Liu,ZC Peng,Z Haoyuan
IF: 5
2003-01-01
Geochimica et Cosmochimica Acta
Abstract:Method and Experiments Mineralogy of the fly ashes were determined by X-ray diffraction. K, Na, Ca, Mg, Cu, Pb and Zn in ashes were determined by ICP-MS and spectrophotometer for As. 15 g fly ash samples (FA1) was placed in 1 L polyethylene bottles and mixed with 1 L of distilled water (pH=7). The bottles were shaken for 24 hours in a horizontal shaker at room temperature. Then, the supernatants were decanted and filtered through a 0.25 um micropore membrane filter at the end of the leaching experiment, and the final pH in leaching solution was measured . The process of the same samples was repeated three times. The higher ratio between the ash and water was to prevent the solution achieving saturation and allowing all the water-soluble fractions in the ashes to be dissolved out. Discussion of results According to chemical composition, the ashes from the study power plants belong to CaO-Fe2O3-Al2O3-SiO2 system. The chemical composition usually fluctuates much due to the different mineral components contained in the coals. The analysis result showed that the content of the main minerals in coal is positive to the chemical and mineral composition of ashes. The trace elements are preferentially concentrated in fly ash, because of its small particles size and large specific surface. So much of K, Na, Ca, Mg and the partial of Pb, Zn, Cu, As, which are adsorbed on the surface of fly ash, are high in concentrations. Therefore, in the ashes of small particle size, the contents of trace elements are high.The leaching test results are shown in Table 3 .From the Table 3, Ca and Na concentrations in the initial leachate are high. Cu, Pb, Zn concentrations were lower than the concentrations of Na, Ca, K and Mg. Zn Shows similar trend to that of Cu, but maintains a constant level. As were generally close to detection limit, but still detectable in all leaching solutions. Such continuous release of Cu, Zn, Pb and As might signify dissolution of the glass in the ash particle. Conclusions The major composition of ashes are SiO2, and Al2O3, low amounts of Fe2O3 and CaO, and little content of SO3, P2O5, Na2O, K2O and TiO2. The leaching behavior of fly ashes indication that the trace elements in the fly ash particles are mainly associated with the surface but some of them are incorporated with the glass matrix as well. Acknowledgements This research was supported by Natural Science Funation of China (40133010, 40273035). The influence of fluid components H2O and CO2 on the partial melting of upper mantle peridotite