Phase behavior of biodegradable poly(L-lactic acid) in supercritical solvents and cosolvents
Uma Sankar Behera,Siddhant Kumar Prasad,Divya Baskaran,Hun-Soo Byun
DOI: https://doi.org/10.1016/j.jcou.2023.102658
IF: 7.7
2024-01-04
Journal of CO2 Utilization
Abstract:Poly(L-lactic acid) (PLLA), a biodegradable polymer from plant sources, is widely employed in biomedical applications for its biocompatibility and versatile mechanical properties. However, comprehending its phase behavior in various solvents poses a challenge for broader applications. In this study, the phase behavior of the polymer was investigated in various solvent and cosolvent media and combinations at a wide range of temperatures and pressures to gain insight into the polymer properties. PLLA of varying intrinsic viscosity (IV): [0.15 dl/g, with an estimated weight average molecular weight (M w ) range of approximately: 1600 to 2400 g/mol; 1.0 dl/g (M w ): 100,000 g/mol); and 1.8 dl/g (M w ): 80,000 to 100,000 g/mol] was employed for this study. The phase behavior of the polymer across different compositions of PLLA and solvent (CH 2 F 2 , CHF 3 , CO 2 , DME, F-22) in a wide range of temperatures from 333 to 425 K and high pressure 1.55 to 172 MPa was investigated. Miscibility of PLLA in DME and F-22 is predicted to be higher with increasing in concentration than the other cosolvents. Furthermore, in the case of the supercritical solvent CHF 3 and DME the phase transition pressure curve of PLLA was observed to exhibit a lower critical solution temperature (LCST) type with a positive gradient with increasing temperature. However, lower phase transition pressure was noticed for lower molecular weight PLLA in supercritical solvent CHF 3 and DME, i.e., of the order IV 0.15 dl/g<iv (iv="" 1.0="" 1.8="" co<sub="" dl="" g)="" g.="" g 2 with increasing the concentration of co-solvent (F-22, DME) from 0 to ∼97 wt% shifted from UCST to LCST type. The LCST curve of PLLA (IV 0.15) in DME intersects with the vapor(V)-liquid(L) curve at T : 353 K and P below 5 MPa, indicating the coexistence of V+L phases.
engineering, chemical,chemistry, multidisciplinary