Crystallographic and magnetic properties of substituted YTi (Fe1−xTx)11

Ying-chang Yang,Sun Hong,Zhang Zhen-yong,Luo Tong,Gao Jian-liang

DOI: https://doi.org/10.1016/0038-1098(88)91094-0

IF: 1.934

1988-01-01

Solid State Communications

Abstract:The substitution effects of Fe with T on magnetic properties of YTi (Fe 1−x T x ) 11 , where T represents Co, Ni, and Si, have been investigated by x-ray diffraction and magnetic measurements. Lattice constants decrease with increasing the content of Co, Ni and Si. Saturation magnetizations were measured with a field of up to 70KOe at 1.5K. Curie temperatures increase monotonically with increasing the content of Co and Ni. A maximum occurs in the variation of saturation moments as a function of concentration in the compounds of YTi(Fe 1−x Co x ) 11 and YTi(Fe 1−x Ni x ) 11 . A change in easy magnetization direction from the c-axis is observed at room temperature in YTi(Fe 1−x Co x ) 11 compounds by increasing the Co content x. Saturation magnetizations and Curie temperatures both decrease with the increasing of Si content.