Abstract:The surface modification of continuous fiber was conducted by the inductive coupling radio frequency cold plasma (ICP) technique. The influence of the plasma parameters, such as treatment time, discharge pressure, power, etc. on the surface chemical composition,surface morphology,surface roughness and surface free energy of continuous fiber was systematically studied by X-ray photoelectron spectroscopy (XPS), atomic force microscopy (AFM) and dynamic contact angle analysis (DCAA), respectively. Results showed that the plasma treatment introduced some polar groups such as 0 C 0 onto the continuous fiber surface, increasing the percentage of surface polar groups; the plasma etched the fiber surface obviously,enhancing the surface roughness and surface free energy and improving the wettability of the fiber distinctly. Plasma treatment conditions should be appropriate during surface modification of fibers by clod plasma. After CF was treated for 5 min,CF surface polar group was increased to a relatively higher level. However,the effect of plasma etching on CF surface is relatively slower. After CF was treated for 5 min,CF surface roughness was changed a little. However, after CF was treated for more than 15 min CF surface roughness was increased significantly. Based on the study above, the interfacial adhesion and fracture mechanism of continuous fiber reinforced soluble polyaromatic ether resin composites was also systematically analysed by interlaminar shear strength (ILSS), water absorption and scanning electron microscopy (SEM) measurements. It was found that CF reinforced poly(phthalazinone ether sulfone ketone) (PPESK) composite interfacial adhesion mechanism analysis indicats that both chemical bonding and mechanical interlocking interaction has a positive effect on composite interfacial adhesion, however, mechanical interaction has a dominant effect on composite interfacial adhesion than chemical bonding interaction. Armos aramid fiber composite interlaminar, shear strength increased from 59. 5 MPa for untreated sample to 68. 8 MPa for plasma treated for 10 min under discharge power at 200 W, with an increase of 15. 6%. The water absorption decrease of composite also indirectly showed that oxygen plasma treatment improved composite interfacial adhesion. The primary failure mode of Armos aramid or PBO/PPESK composites shifted from interface failure to matrix fracture after oxygen plasma treatment. The interfacial adhesion of Armos aramid or PBO/PPESK composites was improved by oxygen plasma treatment due to the chemical linkage and mechanical bonding between Armos aramid or PBO fibers and PPESK matrices, and the chemical linkage effect exhibits more contribution than the mechanical bonding.

Aramid fiber treated by air plasma and its adhesion property with natural rubber/emulsion styrene-butadiene rubber

A promising method for promoting interfacial adhesion of aramid/rubber composite using atmospheric pressure plasma surface modification

Surface Modification of Aramid Fiber by Plasma Induced Vapor Phase Graft Polymerization of Acrylic Acid. I. Influence of Plasma Conditions

X-ray Photoelectron Spectroscopic Analysis of Surface Modification of Aramid Fiber by Low Temperature Plasma

Effect of nitrogen plasma treatment on adhesion of aramid cord to rubber

Wetting and Adhesion Behavior of Armos Fibers after Dielectric Barrier Discharge Plasma Treatment

Effect of plasma treatment on interface of aramid cord/rubber composites

Surface Treatment of Aramid Fiber by Air Dielectric Barrier Discharge Plasma at Atmospheric Pressure

The effect of atmospheric‐pressure air plasma discharge power on adhesive properties of aramid fibers

Effects of Air Plasma Modification on Aramid Fiber Surface and Its Composite Interface and Mechanical Properties

INTERFACIAL STUDIES OF CONTINUOUS FIBERS REINFORCED POLY(AROMATIC ETHERS) CONTAINING PHTHALAZINONE MOIETIES

Influence of Oxygen Plasma Treatment on Surface Properties of Armos Fiber

Surface modification of aramid fiber by crystalline polyarylene ether nitrile sizing for improving interfacial adhesion with polyarylene ether nitrile

Argon Low-Temperature Plasma Modification of Chopped Aramid Fiber and Its Effect on Paper Performance of Aramid Sheets

Surface modification of armos fibers with oxygen plasma treatment for improving interfacial adhesion with poly(phthalazinone ether sulfone ketone) resin

Effects of Plasma Modification of Hybrid Kevlar/PTFE Fabric Surface on Adhesive and Tribological Properties

The analysis of Armos fibers reinforced poly(phthalazinone ether sulfone ketone) composite surfaces after oxygen plasma treatment

Effects of Argon Plasma Treatment on the Adhesion Property of Ultra High Molecular Weight Polyethylene (UHMWPE) Textile

Enhanced interfacial adhesion of aramid fiber reinforced rubber composites through bio‐inspired surface modification and aramid nanofiber coating

Interface Characteristic Of Aramid Fiber Reinforced Poly(Phthalazinone Ether Sulfone Ketone) Composite

Improvement of interfacial adhesion for plasma-treated aramid fiber-reinforced poly(phthalazinone ether sulfone ketone) composite and fiber surface aging effects