Abstract:The wear and adhesion of bearing surface under boundary lubrication is the key to the development and application of bearing technology. For improving the antifriction and antiadhesion properties of the bearing materials, the sulfur rich nano self-lubricating thin layers were prepared on the bearing surface by low-temperature sulfide permeation technology. The morphology and composition of the sulfurized layer were characterized microscopically, and the tribological properties of the sulfurized layer were analyzed to reveal the anti-friction and anti-adhesion mechanism of the sulfurized layer on the surface of bearing steel. The results show that the sulfurized layer is flatter and does not contain nanostructures when the formulation does not contain thiourea, and the content of element S is lower. After the addition of thiourea, the surface of the sulfurized layer is formed by the accumulation of nanosheet-like structures. The nano sulfurized layer has higher S-element content and better tribological properties. When thiourea and tartaric acid are added to the sulfurizing formula at the same time, the nano-sheet structure of the sulfurized layer is more dense and uniform. Moreover, the number of microcracks in the sulfurized layer is small, and the tribological properties are further improved. At the same time, the sulfide in the self-lubricating thin layer and the lubricating oil stored in the gaps can make the bearing surface have a typical "liquid-solid synergistic lubrication effect". That is conducive to the formation of the self-lubricating film and the transfer to the dual parts. All these factors improve the antifriction and antiadhesion properties of the bearing materials effectively.

Lubricating Mechanism of Sulfurized Olefin on Ni-P Brush Plating Layer

Lubricating mechanism of sulfurized olefin on Ni-base brush plating layers

Study of the Lubrication Mechanism of Olefin Sulfide

The Effect of Solid-Liquid Composite Lubrication on the Tribological Properties of Bearing Steel

Tribological performance analysis of nano-FeS films deposited on the surface of bearing steel

Friction and wear behaviour of Sialon/ (Ca,Mg)-Sialon with lubrication by coated PbS nanoparticles as oil additives

Ionic Liquid Lubrication of Electrodeposited Nickel–si3n4 Composite Coatings

Study of the Tribological Properties of Porous ZnS Nanosheets as Lubricating Oil Additive

The Wear Resistance of an Ni-Cu-P Brush Plating Layer on Different Substrates

THE WEAR BEHAVIOR OF BRUSH-PLATED Ni-W-Co/SiC COMPOSITE LAYER WITH OIL LUBRICATION

A Study on the Tribological Properties of Sulfide Layer Produced by Ion Sulphurization

The Synergistic Effects of EP and AW Additives with a Sulphurised Steel Surface under Boundary Lubrication

The Synergistic Effects of EP and AW Additives with Oxynitrided Surface of Steel

Preparation and properties of FeS/iron-based self-lubricating materials by chemical nickel plating-mechanical alloying

The Synergistic Effects of Oil Additive Sulphurized Olefin with Chemico-Thermal Treatment Surfaces of Steel

Synergetic effect between the surface treated with ion nitriding and extreme pressure-antiwear additives under boundary lubrication

Tribological Properties and Mechanisms of Sulfide Layer Prepared by Glow Discharge

Effect of Sulphide Layers on the Tribological Behavior of Steels under Boundary Lubrication Conditions

Effect of structure of ZnO and SiO 2 core-shell composite nanoparticles as lubricant additive on tribological properties of greases

Tribological Performance of Sulfonamide Derivatives As Lubricating Oil Additives in the Diester

Study on the Synergistic Effect between the Plasma Nitrided Steel Surface and Different Lubrication Additives