Characterization of precipitate phases in a Mg–Dy–Gd–Nd alloy

Dehui Li,Jie Dong,Xiaoqin Zeng,Chen Lu,Wenjiang Ding

DOI: https://doi.org/10.1016/j.jallcom.2006.08.059

IF: 6.2

2007-01-01

Journal of Alloys and Compounds

Abstract:Precipitated phases in a Mg–Dy–Gd–Nd alloy during ageing were studied by using transmission electron microscopy. Observations were performed along some orientations parallel to 〈0001〉α and/or 〈112¯0〉α zone axes of the matrix. Results show that the alloy has a rapid ageing response, which can be attributed to the rapid formation of β″ precipitates, occurring in three {112¯0}α planes with DO19 structure; the decreasing of hardness may result from the forming of β1, which forms in three {11¯00}α plates, and the orientation relationship between β1 and the matrix may be described by {11¯1}β1//{112¯0}α, 〈110〉β1//〈0001〉α; further ageing leads to the formation of β precipitates, which also forms as plates parallel to {11¯00}α, and the orientation relationship between β and the matrix phase is identical to that observed between β1 and matrix phase.