Abstract:Nano carbon black used as carbon source for commercial reaction-bonded silicon carbide ceramics leads to much residual silicon, complex shape of silicon islands and low mechanical properties. In order to decrease the residual silicon content, refine the structure and improve the mechanical properties, chopped carbon fibers with high carbon density used as carbon source and fine boron carbide particles with excellent mechanical properties were introduced into the reaction bonded silicon carbide composite. The effects of different volume fractions of fibers and boron carbide on the density, mechanical properties and microstructure have been researched. The results show that carbon fibers have a complete reaction at 1600 degrees C. Carbon fibers with high carbon density have a larger volume expansion during siliconized reaction, which decreases the residual silicon content. By diffusion reaction, carbon fibers control the distribution of residual silicon (fiber-like extensions), which prevents the silicon island from being formed. The introduction of boron carbide ensures the free infiltration and the edge reacted with silicon to form SiC and the ternary phase. It provides part of carbon source. B4C particles pulled up from the matrix in the fracture process, which increases the crack growth distance and improves the energy consumption. It improves the mechanical properties of the composite. When the volume fraction of carbon fiber is 40%, flexural strength and fracture toughness of the composite are the highest, reaching 465 MPa and 7.5 MPa.m(1/2), respectively.

Morphology and Reinforcing Behavior of Short Carbon Fiber in Reaction Bonded Silicon Carbide

Random Chopped Fibers in Reaction Bonded SiC Composite: Morphology, Etching and Reinforcing Properties

Toughening Mechanism Of Short Carbon Fiber Reinforced Reaction Bonded Silicon Carbide Composite Ceramic

Combined Strengthening Mechanism Of Carbon Fiber/Boron Carbide In Reaction Bonded Silicon Carbide Ceramic

Effect of Carbon Particle and Carbon Fiber on the Microstructure and Mechanical Properties of Short Fiber Reinforced Reaction Bonded Silicon Carbide Composite

Microstructure and Mechanical Properties of the Reaction-Sintered Silicon Carbide Ceramics Modified by Carbon Fiber

Effects of Random Chopped Fiber on the Flexural Strength and Toughness of Reaction Bonded Silicon Carbide Composite

Fabrication and Mechanical Properties of SiC Reinforced Reaction-Bonded Silicon Nitride Based Ceramics

Fabrication and characterization of random chopped fiber reinforced reaction bonded silicon carbide composite

Fabrication, Microstructure and Mechanical Properties of Silicon Carbide Short Fiber/Si3N4p-Reinforced BAS composites

Morphology of Sic Whisker in Whisker Reinforced Reaction Bonded Sic Composite

Microstructures and mechanical properties of carbon fiber reinforced silicon nitride composites prepared by gel-casting

Properties of reaction-bonded SiC/Si3N4 ceramics

Mechanical Properties of Reaction-Bonded Si3n4/Sic Composite Ceramics

Preparation and mechanical behaviors of multiscale SiC nanowires/carbon fiber reinforced silicon oxycarbide ceramic composites

Effect of BN interfacial layer on the mechanical behavior of SiC fiber reinforced SiC ceramic matrix composites

Processing, microstructure, and mechanical properties of chopped SiC fibers reinforced ZrB2–hBN–based composites

Zirconia Reinforced Reaction Bonded Silicon Carbide Composites: Microstructure and Mechanical Properties

Effect of the Addition of Carbon Fibres on the Microstructure and Mechanical Properties of Reaction Bonded B4C/SiC Composites

Foldcore Sandwich Structure Formed by BN-coated Graphene Nanosheets Grafted to SiC Fibers with Enhanced Mechanical Performance

Fabrication and Characterization of a New-Style Structure Capillary Channel in Reaction Bonded Silicon Carbide Composites