Abstract:Fly ash (FA) contents and water-binder ratio ( w / b ) are the important factors influencing the mechanical characteristics of cement-based materials, meanwhile the porous structure of material plays a vital role. The compressive strength and water permeability of cement-based samples with high-volume FA contents (0%, 30%, 40%) and different w / b (0.3, 0.4, 0.5) were measured. The results demonstrated that higher FA contents or greater w / b led to lower compressive strength and higher water permeability at an early stage. The pore structure features of samples were obtained using mercury intrusion porosimetry and low-temperature nitrogen gas adsorption (LT-NGA). The pore size distributions (PSDs) and the matrix compressibility in cementitious materials were also analyzed, with the compression coefficient K C ranging from 11.919 to 1.249 × 10 −4 MPa −1 . Increasing the FA content and reducing the w / b resulted in an optimized pore structure of the samples, characterized by changing the main pore type from mesopores (10–50 nm) to micropores (< 10 nm). The pores and fractures in the samples also had distinct multifractal characteristics. The strongest negative correlation between the compressive strength and the width of the multifractal generalized spectrum was proved by Pearson correlation analysis, and the correlation coefficient ( ρ ) was − 0.93. Furthermore, the water permeability had the strongest positive correlation with porosity, with ρ of 0.91. The content of macropores (50–10 μm) had greater influence on its macroscopic properties. The dense structure accompanied by homogeneous PSDs is advantageous for enhancing the strength and anti-permeability properties of cement-based materials.

Study on Relationship Between Properties and Porosity of Concrete with High Amount Fly Ash and Slag on Site

Study on the Effect of Fly Ash and Polycarboxylic Acid Water Reducer on the Properties of Recycled Concrete

Study on performance of high strength pumping concrete compounded by fly ash composite powder under low water-cement ratio

Measurement of Permeability and the Correlation Between Permeability and Strength of Pervious Concrete

Microstructure of the concrete with high volume of fly ash-at the long-term age

Study on Mechanics Property Experiments of High Fly Ash Content Concrete

Quantitative study on the influence of fly ash content, saturation degree and interface transition zone on the permeability of cement-based materials

An Experimental Study on Relationship among Water Sorptivity, Pore Characteristics, and Salt Concentration in Concrete

Mechanical and Hydraulic Behaviors of Eco-Friendly Pervious Concrete Incorporating Fly Ash and Blast Furnace Slag

Research on Some Properties of Fly Ash Concrete with Nano-CaCO3 Middle Slurry

Experimental Study on the Cracking Resistance at Early Ages of High Performance Concrete Added with Lithium Slag and Fly Ash

Resistivity Characters of Concrete with Fly Ash and Slag

lnfluence of steel slag - superfine fly ash composite mineral admixture on the properties of concrete

Role of Artificial Aggregates of Fly Ash and Slag Concretes At Different Water-To-Cement Ratios in Mechanical and Permeability Behavior

Research on Improving Cementitious Material Properties by Adding FineFly Ash

Effects of pore water saturation on the mechanical properties of fly ash concrete

Study on the Physic-mechanical Properties of Concrete Added with Sewer Sludge

Experimental Investigation and Numerical Model for Chloride Diffusivity of Long-Age Fly Ash Cement Slurry

Durability Properties of Structural Concretes Containing Secondary Cementitious Materials

Theoretical investigation on elastic property evolutions of low volume fly ash concrete

Strength, Permeability and Multiscale Pore Characteristics of Cement-Based Materials with High-Volume Fly Ash Contents and Different Water-Binder Ratios