Abstract:Multiple cracking, if formed in an inherently brittle cementitious composite, remarkably boosts its ductility and leads to the desired strain hardening material during tension. The key to predicting multi-crack growth and, ultimately, tuning the composite's tensile properties primarily lies in resolving the competitive propagation of closely spaced microcracks, strung by fibers. A mechanism-based multiphase approach is developed, enabling clarification of the realistic multiple microcracks bridging mechanism arising from the stacked fiber bundles within strain hardening cementitious composites. The proposed multiphase configuration framework establishes reliable models for bridging fiber bundles, interface constitution and matrix cracks, which are critical in all types of fractures, and confronts new challenges arising from competitive opening of stringing cracks. The study has the following novelties: (1) Regarding matrix cracking, a new damage plastic interface model is proposed to characterize the stiffness degradation and gradual recovery of contact stiffness for cementitious composites during cyclic loading. (2) Targeting the crack resistance effect, a unified nonlinear bond-friction model is formulated which is able to capture the elastic bond breaking, friction hardening, fiber rupture, fiber pullout and the cyclic loading behavior of the fiber/matrix interface, simultaneously. (3) Considering the snubbing effect that is intrinsic to cracks, a two-stage evolution algorithm for the fiber bridging force is implemented which distinguishes the bridging efficiency in an intact and cracked medium. We accurately predict the tensile cracking and capture the strain hardening of composites with individual constituent properties, providing further microscopic effects beyond the experimental scope, such as the fiber and matrix stress distributions, through which the development of residual compressive traction in matrix cracks is identified for the first time. This work could serve as a new guide for designing strain hardening cementitious composites with optimal performances.

Multiscale Material Design and Crack Path Prediction of a Polymer-Modified Cementitious Cover Layer

Systematical Calibration and Validation of Discrete Element Models for Fiber Reinforced Cement Treated Aggregates

Predicting Fatigue Damage Growth in Cement-Treated Base Layer Built with Construction and Demolition Waste

A Novel Approach for the Mechanical Response of Cement Concrete Pavement Structure Considering the Interlaminar Interface Shear Slip Effect

Multiscale Prediction of Thermal Damage for Hybrid Fibers Reinforced Cementitious Composites Blended with Fly Ash at High Temperatures

Improvement of boundary effect model in multi-scale hybrid fibers reinforced cementitious composite and prediction of its structural failure behavior

Multi-scale Structure of In-Situ Polymerized Cementitious Composites with Improved Flowability, Strength, Deformability and Anti-Permeability

A novel multi-scale model for predicting the thermal damage of hybrid fiber-reinforced concrete

A Mesoscale Modelling Approach Coupling SBFEM, Continuous Damage Phase-Field Model and Discrete Cohesive Crack Model for Concrete Fracture

Reinforcement Design of Composite Pavement Continuously Reinforced with Basalt Fiber Reinforced Plastics Bars

A Cyclic Plastic-Damage Multiphase Model for Evaluation of Multiple Cracking in Strain Hardening Cementitious Composites

Multiscale Analysis of Concrete Damage and Crack Propagation Under High Cycle Loading

Multiscale Modeling of Elastic Modulus Across Micro-Meso-Macroscales Based on Grid-Nanoindentation Test for Cementitious Materials

Multi-scale Fiber Bridging Constitutive Law Based on Meso-Mechanics of Ultra High-Performance Concrete under Cyclic Loading

Experimental Study and Finite Element Analysis on the Modification of Fast-Hardening Polymer Cement Composite Material Applied to the Anchorage Zone of Expansion Joint

Multiscale simulation of mechanical properties and microstructure of CNT-reinforced cement-based composites

A Mesoscopic Simulation for the Early-Age Shrinkage Cracking Process of High Performance Concrete in Bridge Engineering

Asphalt Layer Cracking Behavior and Thickness Control of Continuously Reinforced Concrete and Asphalt Concrete Composite Pavement

A New Insight to Investigate the Strain Distribution, Evolution, and Crack Development of Cement-Stabilized Coral Aggregate

An atomistic based continuum level 3D mode-I meso-fracture criterion for cement-based concrete

A Multiscale Model for Mechanical and Fracture Behavior of Calcium-Silicate-Hydrate: From Molecular Dynamics to Peridynamics