Abstract:Plasma nitriding is widely used in various industrial applications to improve surface hardness and wear properties. Especially for tool steels, it is also used to improve the support and adhesion of diamond-like carbon (DLC) coatings. The properties of the nitrided zone produced by plasma nitriding are influenced by the applied process parameter, in particular temperature and time. However, for high-alloy tool steels, a deeper understanding of the underlying diffusion processes of the nitrogen and the interaction with the existing microstructure, as well as the effects on the case depth is still lacking. Therefore, in this study, specimens of high-alloy tool steel X153CrMoV12 were plasma nitrided at varying temperatures (480 °C, 520 °C, 560 °C) and treatment times (2 h, 4 h, 16 h). The resulting nitrided zones were investigated by optical and scanning electron microscopy (OM and SEM), depth-dependent glow discharge optical emission spectroscopy (GDOES), X-ray diffraction (XRD), and hardness measurements to characterize their microstructure, chemical composition, and hardness depending on the process parameters. The distribution of carbides (M7C3), e.g., chromium carbides, affects the diffusion of the nitrogen and the layer growth. An increase of temperature and duration leads to an increased layer thickness. The composition of the compound layer is, e.g., influenced by the process parameters: ε nitrides (Fe2–3N) occurred preferentially at lower temperatures, while γ′ nitrides (Fe4N) appeared mostly at higher temperatures. In order to investigate the influence of the carbides of the high-alloy tool steel on the nitriding process, a new methodology was developed by means of finite element analysis (FE), which makes it possible to analyze this influence on the development of the nitrogen concentration profile. This methodology makes it possible for the first time to map the heterogeneous nitrogen evolution and distribution.

Testing of Nitride Case Depth after Gas Nitriding Processing

Study on Gas Nitriding Process of GH4169 Alloy

Nitriding layer depth detection based on mixing frequency nonlinear ultrasonic parameters

Measuring Depth-Dependent Residual Stresses in Gaseous Nitrided Steels Using Indentation Method

Gas nitriding of inner surfaces of deep holes

Enhancing Heavy Load Wear Resistance of AISI 4140 Steel Through the Formation of a Severely Deformed Compound-Free Nitrided Surface Layer

Microstructural and tribological characterization of plasma- and gas-nitrided 2Cr13 steel in vacuum

Nano- and Microhardness Distribution in the Carburized Case of Nb-Microalloyed Gear Steel

Material Influence on the Micropitting and Wear Resistance of Nitrided External and Internal Gears

Evolution of Microstructure and Hardness of the Nitrided Zone during Plasma Nitriding of High-Alloy Tool Steel

Effect of nitrided-layer microstructure control on wear behavior of AISI H13 hot work die steel

Comparison of physical, mechanical and chemical properties of barrel steel 32CrMoV12-10 and nitriding steel 31CrMoV9 after nitriding in gas

Research Progress of Gas Soft-nitriding Technology

MODIFICATION OF TRIBOLOGICAL CHARACTERISTICS OF METALS AFTER NITROGEN IMPLANTATION

Effect of Plasma Nitriding Pretreatment on the Mechanical Properties of AlCrSiN-Coated Tool Steels

Kinetics analysis and enhancement mechanism of aluminum-enhanced plasma nitriding for 42CrMo steel

Mathematical Modelling and Computer Simulation of Nitriding

High Temperature Gas Nitridation and Wear Resistance of TiAl Based Alloys

Effect of Post-Plasma Nitrocarburized Treatment on Mechanical Properties of Carburized and Quenched 18Cr2Ni4WA Steel

Optimized Compound Layer Design for Highly Loaded Nitrided Gears

Study on Low Temperature Gas Multielement Co-penetration on Alloy Carburizing Steel Surface