Material Loss Due to Two Fatigue Cracks Growth in Coalescence Between Two Holes in Aluminum-Alloy Strip

王芳文,陈宜亨

DOI: https://doi.org/10.3321/j.issn:0253-987x.2009.03.026

2009-01-01

Abstract:This paper is one of a series of studies for the coalescence between two neighborly located holes in an aluminum-alloy strip under cyclic tensile loadings.Under some conditions,two initial fatigue cracks were found to nucleate at each hole's rim in the center region between the two holes,where the stress concentration is much more violent than that in other positions.These two cracks grew simultaneously and leaded to the coalescence of the two holes.Thus,a large material loss occurred in the center region between the two holes.Only after the material loss completed,the two outside fatigue cracks tended to grow at the outside rims of the two holes until final failure occurs.This is a new phenomenon,which is difficult to be explained with the classical theories.