Controllable Fabrication of Copper Phthalocyanine Nanostructure Crystals.
Fangmei Liu,Jia Sun,Si Xiao,Wenglong Huang,Shaohua Tao,Yi Zhang,Yongli Gao,Junliang Yang
DOI: https://doi.org/10.1088/0957-4484/26/22/225601
IF: 3.5
2015-01-01
Nanotechnology
Abstract:Copper phthalocyanine (CuPc) nanostructure crystals, including nanoflower, nanoribbon, and nanowire, were controllably fabricated by temperature gradient physical vapor deposition (TG-PVD) through controlling the growth parameters. In a controllable growth system with carrier gas N2, nanoflower, nanoribbon, and nanowire crystals were formed in a high-temperature zone, medium-temperature zone, and low-temperature zone, respectively. They were proved to be β-phase, coexist of α-phase and β-phase, and α-phase respectively based on x-ray diffraction results. Furthermore, ultralong CuPc nanowires up to several millimeters could be fabricated by TG-PVD without carrier gas, and they were well-aligned to form large-area CuPc nanowire crystal arrays by the Langmuir-Blodgett method. The nanostructure crystals showed unusual optical absorption spectra from the ultraviolet-visible to near-infrared range, which was explained by the diffraction and scattering caused by the wavelength-sized nanostructures. These CuPc nanostructure crystals show potential applications in organic electronic and optoelectronic devices.