Abstract:A vertically aligned Pd nanowire array was successfully fabricated on an Au/Ti substrate using an anodic aluminum oxide (AAO) template by a direct voltage electrodeposition method at room temperature using diluted neutral electrolyte. The fabrication of Pd nanowires was controlled by analyzing the current–time transient during electrodeposition using potentiostat. The AAO template and the Pd nanowires were characterized by scanning electron microscopy (SEM), energy-dispersive X-ray (EDX) methods and X-Ray diffraction (XRD). It was observed that the Pd nanowire array was standing freely on an Au-coated Ti substrate after removing the AAO template in a relatively large area of about 5 cm2, approximately 50 nm in diameter and 2.5 μm in length with a high aspect ratio. The nucleation rate and the number of atoms in the critical nucleus were determined from the analysis of current transients. Pd nuclei density was calculated as 3.55 × 108 cm−2. Usage of diluted neutral electrolyte enables slower growing of Pd nanowires owing to increase in the electrodeposition potential and thus obtained Pd nanowires have higher crystallinity with lower dislocations. In fact, this high crystallinity of Pd nanowires provides them positive effect for sensor performances especially.A vertically aligned Pd nanowire array was successfully fabricated on an Au/Ti substrate using an anodic aluminum oxide (AAO) template by a direct voltage electrodeposition method at room temperature using diluted neutral electrolyte. The fabrication of Pd nanowires was controlled by analyzing the current–time transient during electrodeposition using potentiostat. The AAO template and the Pd nanowires were characterized by scanning electron microscopy (SEM), energy-dispersive X-ray (EDX) methods and X-Ray diffraction (XRD). It was observed that the Pd nanowire array was standing freely on an Au-coated Ti substrate after removing the AAO template in a relatively large area of about 5 cm2, approximately 50 nm in diameter and 2.5 μm in length with a high aspect ratio. The nucleation rate and the number of atoms in the critical nucleus were determined from the analysis of current transients. Pd nuclei density was calculated as 3.55 × 108 cm−2. Usage of diluted neutral electrolyte enables slower growing of Pd nanowires owing to increase in the electrodeposition potential and thus obtained Pd nanowires have higher crystallinity with lower dislocations. In fact, this high crystallinity of Pd nanowires provides them positive effect for sensor performances especially.

Fabrication of organic copper phthalocyanine nanowire arrays via a simple AAO template-based electrophoretic deposition

Optical Device Based on a Nanopillar Array by the Pattern Transfer of an Anodic Aluminum Oxide Membrane

G030084 Fabrication of High Density Cu Nanowire Array by Template Method and Its Evaluation

J212025 Fabrication of Nanowire Surface Fastener on Flexible Substrate and Its Electrical and Mechanical Properties

Highly Photoconductive Copper Phthalocyanine-Coated Titania Nanoarrays Via Secondary Deposition

Fabrication of vertically aligned Pd nanowire array in AAO template by electrodeposition using neutral electrolyte

Creating In‐Plane Metallic‐Nanowire Arrays by Corner‐Mediated Electrodeposition

Thin Films of Porphyrin-Perylene Molecular Array Fabricated by Electrophoresis Methodology

Fabrication of gadolinium biphthalocyanine nano/microwires by electrophoretic deposition

T0301-1-1 Fabrication of Au Nanowire Utilizing Porous Aluminum

Cu Oxide Nanowire Array Grown on Si-based SiO2 Nanoscale Islands Via Nanochannels

Fabrication of a novel copper phthalocyanine/titania nanocomposite film and its photoconductive properties

Fabrication of Anodic Aluminum Oxide Template and Cu Nanowire Surface Fastener

One-Step Fabrication of Copper Nanopillar Array-Filled AAO Films by Pulse Electrodeposition for Anisotropic Thermal Conductive Interconnectors

Fabrication and Electrical Properties of a Cu–tetracyanoquinodimethane Nanowire Array in a Porous Anodic Alumina Template

Preparation And Characterization Of Cuo Nanowire Arrays

In Situ Synthesis of Poly(Copper Phthalocyanine) Nanostructures for Organic Nanodevices

Controllable Template Synthesis of Ni/Cu Nanocable and Ni Nanotube Arrays: a One-Step Coelectrodeposition and Electrochemical Etching Method.

Fabrication of Nanowire-Like Cuprous Oxide in Aqueous Solutions of a Triblock Copolymer

Synthesis and optical properties of poly[3-(2-methoxyphenyl)thiophene] nanowires confined in porous anodic alumina membrane

Electrochemical Synthesis of Copper Nanowires