Abstract:The multiferroic Co/Co3O4/PZT composite films are prepared on Pt/Ti/SiO2/Si wafers by sol-gel process combined with pulsed laser deposition method. The phase structures, microstructural topographies and element valence states of the composite films are characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and X-ray photoelectron spectrum (XPS). The ferroelectric, electrical and magnetic properties as well as the magnetoelectric coupling behaviors are measured, and the exchange bias effect and its influence on the magnetoelectric coupling behavior of the composite film are studied systematically. The results show the composite films have well-defined ferroelectric hysteresis loops with a remanent polarization value of similar to 17 mu C/cm(2). The composite film exhibits evidently an exchange bias effect. Typically, a exchange bias field of similar to 80 Oe is observed at 77 K. Both the exchange bias field and magnetic coercive field increase with reducing the temperature. The exchange bias field increases to 160 Oe when the temperature decreases to 10 K. The XPS results confirm that an about 5 nm-thick CoO layer appears at the Co/Co3O4 interface due to the oxygen diffusion during the preparation, indicating that the exchange bias effect at 77 K is caused by the pinning effect of the antiferromagnetic CoO layer while the exchange bias effect at 10 K originates from the combining effect of antiferromagnetic CoO and Co3O4 layers. The measurement results of magnetocapacitance versus magnetic field curves at different temperatures show that the composite films have remarkable magnetoelectric coupling properties. The response of capacitance to temperature changes with the variation of external magnetic field. Further investigations show that the composite film possesses distinct anisotropic magnetocapacitance effect. When the direction of the magnetic field changes, the magnetocapacitance of the composite film changes from positive value to negative value. Moreover, the magnetocapacitance value changes with the variations of temperature and magnetic field magnitude. Typically, at 300 K a maximum value of positive magnetocapacitance (5.49%) and a minimum value of negative magnetocapacitance of (1.85%) are obtained at 4000 and 4000 kOe, respectively. When the temperature is reduced to 10 K, the positive magnetocapacitance decreases to a minimum value (0.64%) while the negative magnetocapacitance increases to a maximum value (5.4%). We perform a detailed analysis on such a magnetoelectric coupling behavior, and elucidate its origin, which should be attributed to the exchange bias effect and interface-mediated magnetism-stress-electricity coupling process.

Ferromagnetism And Exchange Bias In A Diluted Magnetic Ferroelectric Oxide

Exchange Bias in (110)-Orientated Bi0.9la0.1feo3/La0.5ca0.5mno3 Films

Room Temperature Ferroelectric, Ferromagnetic and Magnetoelectric Properties of Ba-Doped Bifeo3 Thin Films

Room-Temperature Ferromagnetism In The Co-Doped Ba0.5sr0.5tio3 Thin Films

Electron engineering of metallic multiferroic polarons in epitaxial BaTiO 3

Exchange bias in (1 1 0)-orientated Bi 0.9La 0.1FeO 3/La 0.5Ca 0.5MnO 3 films

Ferroelectric and magnetic properties of Dy-doped BaTiO3 films

Charge-Transfer-Induced Interfacial Exchange Coupling at the Co/BiFeO3 Interface

Ferrimagnetism and Abnormal Spin Lattice Coupling in Dilute Magnetic Ferroelectric (bi 0.46 Na 0.46 Ba 0.08 )tio 3 :Co

Antiferromagnet thickness dependence and rotatable spins in exchange biased CoO/Fe films

Room-temperature Electric Control of Exchange Bias Effect in CoO1 – Δ/co Films Using Pb(Mg1/3Nb2/3)0.7Ti0.3O3 (110) Substrates

Correlation between the multiferroic properties in (1-x)BaTiO3-xCoFe2O4 composites

Room-temperature electric control of exchange bias effect in CoO<sub>1 – δ</sub>/Co films using Pb(Mg<sub>1/3</sub>Nb<sub>2/3</sub>)<sub>0.7</sub>Ti<sub>0.3</sub>O<sub>3</sub> (110) substrates*

Room-temperature Ferromagnetism and Ferroelectricity in Fe-dopedBaTiO3

Exchange bias effect and magnetoelectric coupling behaviors in multiferroic Co/Co3O4/PZT composite thin films

Study of Multiferroic Properties in Bi5Fe0.5Co0.5Ti3O15 Thin Films

Exchange Bias in Tetragonal-Like BiFeO3/Sr2FeMoO6 Bilayer

Multiferroic Properties of Ba2+-Ti4+ co-doped YFeO3 Ceramics

Strain Induced Magnetoelectric Coupling Between Magnetite and BaTiO3

The Effects of Co-Ti Co-Doping on the Magnetic, Electrical, and Magnetodielectric Behaviors of M-Type Barium Hexaferrites

Temperature dependence of magnetic anisotropy and domain wall tuning in BaTiO3(111)/CoFeB multiferroics