Electrochemically deposited calcium phosphate/lithium coating

Wang Jia-wei,Zhou Yi

2009-01-01

Abstract:BACKGROUND: Lower concentration of lithium ion (4 mmol/L) can stimulate Wnt gene signal and promote caryocinesia and proliferation of human mesenchymal stem cells. OBJECTIVE: To prepare the electrochemically co-deposited calcium phosphate/lithium coating, by which to learn the effects of lithium on the attachment and proliferation of MG63 osteoblast-like cells. DESIGN, TIME AND SETTING: Contrast study was performed at Key Laboratory for Oral Biomedical Engineering of Ministry of Education, Medical School of Stomatology, Wuhan University from March to December 2007. MATERIALS: Ti6Al4V plates with 1 cm diameter and 1 mm thickness were provided by Shanxi Dechang Titanium and Nickle Co., Ltd.; LiCl was provided by EMD Biosciences, USA; MG63 cells were provided by Wuhan University Typical Culture Collection Center. METHODS: Two concentrations of lithium (0.5 g/L and 5 g/L) were added in calcium phosphate electrolytes. Thereafter, calcium phosphate coatings were deposited on the titanium alloy cathode. All coatings were observed with scanning electron microscopy, and determined with X-ray diffraction and Fourier transform infrared spectroscopy. The lithium content was measured with atomic absorption spectrum, and its release profile was monitored in simulated physiology solution. The cell attachment and proliferation of MG63 osteoblast-like cells were determined through a Cell Counting Kit-8. MAIN OUTCOME MEASURES: Surface microstructure, composition, thickness and lithium content of the coatings, as well as the attachment and proliferation status of MG63 cells on the coatings. RESULTS: The addition of lithium inhibited the deposition of calcium phosphate coating. With the increasing concentration of lithium in the electrolyte, the surface of calcium phosphate coating became flatter, and the crystals became smaller. In addition, an increasing content of octacalcium phosphate could decrease content of phosphorite and coating thickness. By 0.5 g/L lithium chloride in the electrolyte, the content of lithium in the coating was 2.2 mg/g; by 5 g/L lithium chloride in the electrolyte, the content of lithium in the coating was 5.5 mg/g. In simulated physiology solution (pH=7.3), the lithium ions presented a burst-releasing profile. Within half an hour, the released lithium ion achieved 70%-80% of final concentration. After 24 hours, the dissolution gradually reached the saturation level. Cell culture test demonstrated that the co-deposited calcium phosphate/lithium coating enhanced the attachment of MG63 osteoblast-like cells. When the concentration of LiCl was 5 g/L, multiplication index of MG63 osteoblast-like cells was significantly increased on the third day (P < 0.05). CONCLUSION: Lithium can be electrolytically co-deposited with calcium phosphate on the titanium alloy surface, which may thus enhance the bioactivity of the coatings.