Enhanced Biocompatibility and Osteogenic Property of Biodegradable Zn-0.5Li Alloy through Calcium–Phosphorus Coating

Haotian Xing,Yunzhi Tang,Xinying Fa,Hongyun Zhang,Zhangzhi Shi,Shenglian Yao,Luning Wang
DOI: https://doi.org/10.3390/coatings14030350
IF: 3.236
2024-03-15
Coatings
Abstract:Zinc and its alloys have garnered significant attention in the field of biological implantation due to their biodegradable, osteogenic, and mechanical properties. However, the degradation of zinc and its alloys always lead to an increase in local ion concentration, and the bare metal surfaces lack biocompatibility for implantation. To address these issues, a layer of calcium–phosphorus (CaP) coating was prepared on the surface of a Zn-0.5Li alloy. The micro-structure of the coating was observed with scanning electron microscopy (SEM) and a white light interferometry microscope. The phases of the coatings were characterized through X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS). The bonding strength between the coating and substrate was investigated using a scratch tester with a diamond stylus, and the corrosion properties were assessed using an electrochemical method. For the evaluation of biocompatibility and osteogenic properties, MC3T3-E1 cells were cultured on the coating. Live/dead staining and proliferation tests were performed to assess cell viability and growth. Cell adhesion morphology was observed with SEM, and the level of alkaline phosphatase (ALP) in the MC3T3-E1 cells cultured on the material surface was evaluated by ALP staining and activity measurement. The CaP coating on the zinc alloy surface improved the alloy's biocompatibility and osteogenic property, and could be a promising surface modification option for a biodegradable zinc alloy.
materials science, multidisciplinary,physics, applied, coatings & films
What problem does this paper attempt to address?
The paper mainly addresses the following issues: ### Research Background and Objectives - **Background**: Zinc and its alloys have garnered extensive attention in the field of biomedical implants due to their biodegradability, osteogenic properties, and mechanical performance. However, the degradation of zinc and its alloys in vivo can lead to elevated local ion concentrations, and the exposed metal surface lacks biocompatibility. - **Objectives**: To overcome the aforementioned issues, researchers prepared a calcium phosphate (CaP) coating on the surface of Zn-0.5Li alloy through a chemical conversion method, aiming to enhance the alloy's biocompatibility and osteogenic properties. ### Main Research Content 1. **Coating Preparation and Characterization**: - CaP coatings with different reaction times were prepared on the surface of Zn-0.5Li alloy using a chemical conversion method. - The microstructure and composition of the coatings were analyzed using techniques such as scanning electron microscopy (SEM), energy-dispersive spectroscopy (EDS), white light interferometry (WLIM), X-ray diffraction (XRD), and X-ray photoelectron spectroscopy (XPS). - The adhesion strength between the coating and the substrate was evaluated using scratch tests. 2. **Corrosion Performance Evaluation**: - The corrosion performance of the coatings was assessed using electrochemical impedance spectroscopy (EIS) and other methods. 3. **Biocompatibility and Osteogenic Evaluation**: - The biocompatibility and osteogenic activity of the coatings were evaluated by culturing MC3T3-E1 cells on the coating surface, including assessments of cell viability, proliferation capacity, adhesion morphology, and alkaline phosphatase (ALP) levels. ### Conclusion - The CaP coating significantly improved the biocompatibility and osteogenic properties of the Zn-0.5Li alloy, showing potential for surface modification of biodegradable zinc alloys. - Increasing the coating thickness further enhanced the corrosion resistance of the alloy. - The Zn-0.5Li alloy treated with the CaP coating exhibited good cell compatibility and osteogenic activity, indicating that this material has the potential to become an excellent orthopedic implant material.