Abstract:Electroplating sludge is a hazardous waste and secondary metal resource because of its heavy metal content, which poses a huge threat to environmental safety if not properly disposed. An innovative process of oxidizing roasting followed by water leaching and smelting reduction to recover Cr, Cu, and Ni from electroplating sludge was proposed in this research, in which other two hazardous wastes of spent cathode carbon combustion dust and copper refining slag were co-treated. The NaF from spent cathode carbon combustion dust could convert Cr2O3 to Na2CrO4 using the oxidizing roasting process, resulting in a Cr recovery through the subsequent water leaching. The Na2CrO4 formation was promoted by CaO owing to it transferring the Cr spinel phase of FeCr2O4 [1+] to CaCrO4 and then to Na2CrO4. Under optimal conditions, the Cr recovery reached 97.1 %, and most ‘F’ was solidified into CaF2. In the next smelting reduction of the leaching residue, the Cu and Ni were recovered mainly in the form of Cu-Ni alloy. The addition of copper refining slag promoted their recovery, due to it modifying the molten slag and alloy structures and increasing the Cu-Ni alloy separation from molten slag. Some generated high-melting-point Cu-Ni-Fe and Ni-Fe alloys were converted to a Cu-Ni alloy with a low melting point in presence of Co from the copper refining slag, simultaneously with which the Fe was transferred out from Cu-Ni-Fe and Ni-Fe alloys and combined with Co to form a Fe-Co alloy. It increased Cu-Ni alloy droplets aggregation from molten slag and decreased their contents in the residual slag. Under optimized conditions, the Cu and Ni contents in the residual slag decreased to 0.37 and 0.06 wt%, respectively. Besides, the residual slag mainly composed of CaO, CaF2 and SiO2 could be used to prepare building materials rendering it harmless.

Recovery of copper from galvanic sludge by reductive roasting combined with acid leaching

Recovery of copper from refining slags of copper fire anode furnace by waste acid leaching and CaO roasting process

Recovery of valuable metals from electroplating sludge with reducing additives via vitrification

Recovery of valuable metals from copper slag

Volatilization of Zn and Pb and Preparation of Integrated Micro-Electrolysis Filter from Copper Slag and Its Application for Removing Cr(VI) from Aqueous Solution.

Recovery of Zinc and Copper from Lead Slag by the Combined Process of Beneficiation and Roasting

Recovery of Zinc and Lead from Copper Smelting Slags by Chlorination Roasting

Innovative technology and mechanism for comprehensive recovery of copper, nickel, zinc and iron in electroplating sludge

Use of complementary peptides and their antibodies in T-cell-mediated autoimmune disease: experiments with myelin basic protein.

Recovery of Copper, Lead and Zinc from Copper Flash Converting Slag by the Sulfurization-Reduction Process

Galvanic sludge metals recovery by pyrometallurgical and hydrometallurgical treatment

Recovery of Valuable Metals from Copper Slag by Hydrometallurgy

Separation and Extraction of Valuable Metals from Electroplating Sludge by Carbothermal Reduction and Low-Carbon Reduction Refining

Stepwise recovery of Ni, Cu, Zn, and Cr: A green route to resourceful disposal of electroplating sludge

Iron and copper recovery from copper slags through smelting with waste cathode carbon from aluminium electrolysis

Thermodynamic analysis and process optimization of zinc and lead recovery from copper smelting slag with chlorination roasting

Process of Chloridizing Roasting-Weak Acid Leaching for Electroplating Sludge

Kinetics Study on the Leaching of Copper from Calcification Roasting Copper Refining Slag Using Waste Acid

Efficient recovery of zinc and copper from copper smelting slag (CSS) by cooperative modification with a composite medium of FeS-O2

Treating waste with waste: Metals recovery from electroplating sludge using spent cathode carbon combustion dust and copper refining slag

Recovery of lead and silver from zinc acid-leaching residue via a sulfation roasting and oxygen-rich chlorination leaching method