The fracture of two-layer leaf spring: Experiments and simulation
Guang Cheng,Kaiyuan Chen,Yu Zhang,Yuanchang Chen,Guang Cheng,Kaiyuan Chen,Yu Zhang,Yuanchang Chen
DOI: https://doi.org/10.1016/j.engfailanal.2021.105971
IF: 4
2022-03-01
Engineering Failure Analysis
Abstract:Leaf spring is often used in commercial vehicles' suspension systems to ensure ride comfort and support dynamic wheel loads. In this study, we found a failure phenomenon in a two-layer leaf spring where the fatigue fracture occurred on the companion spring leaf. The decarbonization layer was observed on the surface of the leaf with a 100 μm thickness. The Vickers hardness of the leaf was reduced from ∼ 550 Hv of the inner material to ∼ 500 Hv at the surface region. The decarbonization layers led to fatigue fracture initiation, propagation, and total failure of the spring. Two-dimensional (2-D) finite element simulations were conducted to illustrate the effects of the decarbonization layer and the surface defects. Also, the fracture process was represented in the three-dimensional (3-D) simulation. We conclude that either additional surface treatments or installing rubber pads between each leaf will be helpful to raise the leaf spring's durability.
engineering, mechanical,materials science, characterization & testing