Abstract:CaWO4 nanocrystals with average diameters of 20–30nm and nanorods with mean lengths of 600–1000nm were controllably synthesized through a facile microemulsion-mediated hydrothermal procedure. And the factors affecting the morphologies of the products, such as the molar ratio (w) between water and CTAB, the reaction temperature and the concentration of the reactants, were studied and discussed. With the increase of the w value, the diameter of the as-synthesized products increased gradually, except in the case of w=10 where nanorods were formed. With the temperature increasing, the morphologies of the products changed from nanocrystals to nanorods, and finally to nanocrystals again. However, the concentration of the reactants exhibited no obvious influence on the shape and size of the CaWO4 product. A possible mechanism is proposed for the selective formation of the different morphologies. The photoluminescent properties of the CaWO4 nanocrystals are also reported. All the products of CaWO4 with different morphologies exhibited the only green peak at 435nm with an excitation wavelength at 238nm.

Low-temperature Synthesis of Metal Tungstates Nanocrystallites in Ethylene Glycol

Preparation And Magnetic Properties Of Cowo4 Nanocrystals

General Synthesis of Single‐Crystal Tungstate Nanorods/Nanowires: A Facile, Low‐Temperature Solution Approach

Low-Temperature Synthesis Of Cdwo(4)Nanorods Via A Hydrothermal Method

Morphology-controlled Synthesis and Characterization of MnWO4 Nanocrystals Via a Facile, Additive-Free Hydrothermal Process

Morphology-controlled Synthesis of CdWO_4 Nanocrystals

Synthesis of CaWO4 Nanoparticles by a Molten Salt Method

Nearly Monodisperse Tungstate MWO4 Microspheres (M = Pb, Ca): Surfactant-Assisted Solution Synthesis and Optical Properties

Low-Temperature Synthesis and Structural Characterization of Single-Crystalline Tungsten Oxide Nanorods

Hydrothermal synthesis of sodium tungstate nanorods and nanobundles in the presence of sodium sulfate

Hydrothermal Synthesis and Characterization of CdWO4 Nanorods

Solvothermal Synthesis and Characterization of Crystalline CaWO4 Nanoparticles

Low Temperature Synthesis of Vanadium Pentoxide Nanocrystallines by Sol-Gel Method

Synthesis of NiWO4 nano-particles in low-temperature molten salt medium

Sonochemical synthesis of PbWO4 crystals with dendritic, flowery and star-like structures

Controllable Synthesis of Hierarchical Nanostructures of Cawo4 and Srwo4 Via A Facile Low-Temperature Route

The synthesis and photoluminescent properties of calcium tungstate nanocrystals

Mono-Disperse CaWO4 Microsphere with Hierarchical Structures: Room Temperature Synthesis and Its Optical Properties

SONOCHEMICAL SYNTHESIS OF PbWO4 NANOPARTICLES

Low‐temperature Synthesis of Tungsten Diboride Powders Via a Simple Molten Salt Route

Low-temperature synthesis and optical properties of wurtzite ZnS nanowires