Abstract:Ceramic coatings with aluminum titanuate (Al2TiO5) were prepared on Ti–6Al–4V alloy using pulsed bi-polar Micro-arc Oxidation (MAO). The micromorphology and phase composition of the micro-arc-oxidition ceramic coatings on the titanium alloy were characterized by X-ray powder diffraction (XRD), and scanning electron microscopy (SEM) respectively. The results revealed that the distinct discharge channels and pores on the surface of the micro-arc-oxidition coatings appeared, and these channels were connected in the molten state. The electrolyte concentration was inversely proportional to the coating hardness; additionally, the coating prepared with sodium aluminate and sodium hypophosphite concentrations of 4 g/L and 0.5 g/L, respectively, was the most refined after high-temperature sintering, and it was demonstrated to better prevent oxidation. Increasing the electrolyte concentration coincided with fluctuating coating thermal shock resistance. The thermal shock resistance of the coating respectively prepared with sodium aluminate, and the sodium hypophosphite concentrations of 4 g/L and 0.5 g/L was the highest. Additionally, the high-concentration coatings performed significantly better than the low-concentration coatings. The oxidation resistance of the coating samples was also significantly higher than that of the TC4 titanium alloy substrate. The adhesion strength between the coatings and the substrate with and without the sealing treatment was measured by tensile tests. Then, the high-temperature oxidation performance of the coating samples with and without the sealing treatment was investigated by conducting a high-temperature oxidation experiment at a calcinating temperature of 500 °C. The results indicate that the adhesion strength between the coatings and substrate was high for the as-prepared and sealed micro-arc oxidation samples regardless of whether they were calcined. The high-temperature oxidation mass increase curves for the sealed and unsealed coating samples calcined at 500 °C for 500 h revealed that the high-temperature-oxidation-induced mass increase of the coating samples sealed with a sodium silicate solution was much lower than that of the titanium alloy substrate. Thus, the sealing treatment significantly improved the high-temperature oxidation resistance of the TC4 titanium alloy. Lastly, the high-temperature oxidation behavior at 500 °C was analyzed and discussed.

Effect of FeSO4 Concentration on the Optical Property of Ceramic Coatings by Micro-Arc Oxidation

Study on Structure and Properties of Microarc Oxidation Coating Formed on AM60B Magnesium Alloy

Effect of Several Inorganic Additives on Microstructure and Properties of Microarc Oxidation Coating on Aluminium Alloy

Effect of Potassium Fluoride in Electrolytic Solution on the Structure and Properties of Microarc Oxidation Coatings on Magnesium Alloy

The Effects of Na2WO4 Concentration on the Properties of Microarc Oxidation Coatings on Aluminum Alloy

Preparation of Micro-Arc Oxidation Ceramic Coating on Aluminum Alloys

Effect of Na2 WO4 on properties of micro-arc oxidation ceramic coatings on aluminum alloy

Study on Microstructure and Properties of Black Micro-Arc Oxidation Coating on AZ31 Magnesium Alloy by Orthogonal Experiment

The Effect of Annealing on Microstructure and High Temperature Erosion Property of Arc-Spraying Coatings Containing Nanosized Ceramic Powders

High-temperature oxidation resistance of ceramic coatings on titanium alloy by micro-arc oxidation in aluminate solution

Effect of ultrasonic field on the friction and oxidation characteristics of FeCrAl Coatings

Influences of Argon Ambience on Phase Composition and High Temperature Oxidation Resistance Property of Ceramic Coatings on Ti Alloy by Micro-Arc Oxidation

Microstructure and High Temperature Oxidation Resistance of FeMnCrAl/Cr3C2 Coatings Deposited by High Velocity Arc Spraying

Study on the Optimization of the Preparation Process of ZM5 Magnesium Alloy Micro-Arc Oxidation Hard Ceramic Coatings and Coatings Properties

Effect of Pre-Anodized Film on Micro-Arc Oxidation Process of 6063 Aluminum Alloy

The effect of micro-arc oxidation time on the structure of the porous titania films prepared by a composite oxidation

Effects of nano-SiO 2 particle addition on the structure and properties of micro-arc oxidation ceramic coatings on 7075 aluminum alloy

Influence of Ferric Oxide Modification on the Properties of Copper Oxide Supported on Γ-Alumina

Preparation and Characterizations of Fe/Ce Oxidation Nano Glass Coatings

The Effect of Surface Modification on the Microstructure and Properties of Γ-Fe2o3 Nanoparticles

Effect of Ultrasonic Vibration on Microstructure and Antifouling Capability of Cu-Modified TiO2 Coating Produced by Micro-Arc Oxidation