Abstract:<section class="article-section__content"><h3 class="article-section__sub-title section1"> BACKGROUND</h3>CO2 reforming of methane, also known as dry reforming of methane, has received significant attention because this technology can convert notorious greenhouse gases (CH4/CO2) into useful syngas (H2/CO). However, this technology still hasn't been commercialized, primarily due to the lack of feasible catalysts. </section><section class="article-section__content"><h3 class="article-section__sub-title section1"> RESULTS</h3>Based on zirconia (ZrO2) nanoparticles with pure monoclinic (m) or tetragonal (t) crystal phase, three nickel (Ni) catalysts (Ni/m‐ZrO2, Ni/t‐ZrO2 and Ni/m‐ZrO2@Al2O3) have been synthesized for CO2 reforming of methane. The Ni/t‐ZrO2 catalyst exhibited lowest reforming activity with CH4 conversion of 15.5% at 700 °C under 1 atm with a gas hourly space velocity (GHSV) of 96 000 mL/(h gcat). The Ni/m‐ZrO2 catalyst showed much higher initial activity but underwent severe deactivation, over which CH4 conversion decreased from 56.1% to 33.4% after 300 min of reaction. The nanocomposite Ni/m‐ZrO2@Al2O3 catalyst with confinement effect possessed the best activity and good stability. Specifically, its CH4 conversion decreased merely from 60.2% to 55.3% after 24 h of reaction. </section><section class="article-section__content"><h3 class="article-section__sub-title section1"> CONCLUSION</h3>Structural characterizations demonstrate that limited specific surface area and weak metal‐support interactions existed on the Ni/t‐ZrO2 catalyst, which led to large Ni nanoparticles and thus poor reforming activity. Both Ni/m‐ZrO2 and Ni/m‐ZrO2@Al2O3 catalysts had high specific surface area and tiny Ni nanoparticles, which may rationalize the high reforming activity. The improved stability on the Ni/m‐ZrO2@Al2O3 catalyst was mainly related to the alleviated carbon deposition endowed by enriched surface basicity and strengthened metal‐support interactions. This article is protected by copyright. All rights reserved.</section>

Small Amounts of Rh-Promoted Ni Catalysts for Methane Reforming with CO 2

Rh Doping Effect on Coking Resistance of Ni/SBA-15 Catalysts in Dry Reforming of Methane

Meso-porous Ni/Mg/Al catalysts for methane reforming with CO2

Production of synthesis gas via methane reforming with CO2 on noble metals and small amount of noble-(Rh-) promoted Ni catalysts

Coke-resistance over Rh–Ni bimetallic catalyst for low temperature dry reforming of methane

Doped Ni Catalysts for Methane Reforming with CO 2

Study on CO2 reforming of methane to syngas over Al 2O3-ZrO2 supported Ni catalysts prepared via a direct sol-gel process

A nanoscale Ni/ ZrO 2 catalyst coated with Al 2 O 3 for carbon dioxide reforming of methane

Carbon Dioxide Reforming of Methane over Ni-based Catalyst

Synthesis of nickel catalysts supported on Zr-doped ordered mesoporous Al2O3 and their catalytic performance for low-temperature CO2 reforming of CH4

Study Of Durable Catalyst For Methane Reforming Using Co2

Improving Anti-Coking Properties of Ni/Al2O3 Catalysts via Synergistic Effect of Metallic Nickel and Nickel Phosphides in Dry Methane Reforming

Investigation of CH 4 Reforming with CO 2 on Meso-Porous Al 2 O 3 -Supported Ni Catalyst

Investigation of CH<sub>4</sub> Reforming with CO<sub>2</sub> on Meso-Porous Al<sub>2</sub>O<sub>3</sub>-Supported Ni Catalyst

Study of Ni-Co-ZrO2/Al2O3 Catalysts for Carbon Dioxide Reforming of Methane at Low CO2

Characterization of Ca-promoted Ni/α-Al2O3 Catalyst for CH4 Reforming with CO2

Durable Ni/Mgo Catalysts For Co2 Reforming Of Methane: Activity And Metal-Support Interaction

Stable Ni/ZrO2 catalyst for carbon dioxide reforming of methane

Preparation adjacent Ni-Co bimetallic nano catalyst for dry reforming of methane

Cobalt-doped Ni-based catalysts for low-temperature CO 2 methanation

Supported Co Catalysts for Methane Reforming with CO2