Study on wear behavior of TiAlN coating on GDL-4 high speed steel

Luo Lai-ma,Liang Yi-long

2008-01-01

Abstract:TiAlN film was coated on GDL-4 high speed steel(HSS) by unbalanced magnetron sputtering ion plating process.The sliding wear tests were carried out on a MMS-2A wear tester.The wear mass loss and friction coefficient were investigated under different loads.The wear mechanism of TiAlN-coated GDL-4 steel was compared with that of TiAlN-coated W6Mo5Cr4V2(M2) steel and uncoated GDL-4 steel.The results show that the wear mass loss and friction coefficient of TiAlN-coated GDL-4 steel are both low and similar to that of TiAlN-coated W6Mo5Cr4V2 steel,obviously less than that of uncoated GDL-4 steel under same loading conditions.The worn surfaces were analysed by SEM.The wear-out failure of TiAlN-coated GDL-4 steel is ascribed to the delamination and slight plastic deformation of the coatings.The wear-out failure of uncoated GDL-4 steel is mainly plough wear.The results indicate the wear resistance of TiAlN-coated GDL-4 steel approaches that of TiAlN-coated W6Mo5Cr4V2 steel.