Abstract:In this study, a phenol–formaldehyde resin–montmorillonite intercalation composite solution was used as a modifier to treat Chinese fir via impregnation and compression. The basic characteristics and wettability of the PF (phenol–formaldehyde)–montmorillonite impregnation solution were analyzed. The effects of the solid content of PF, the quantity of montmorillonite, and the impregnation time on the impregnation weight gain of Chinese fir were studied through orthogonal experiments. The results showed that when the amount of montmorillonite was 1%, the wettability of the PF–montmorillonite impregnation solution performed the best, the curing time was short, and the curing strength was high. The optimal impregnation process consists of a PF solid content of 25%, an impregnation time of 120 min, and a montmorillonite ratio of 1%. Under these conditions, the modified Chinese fir was prepared via hot pressing. The effects of the addition of montmorillonite and different levels of compressibility on the physical and mechanical properties of modified wood were studied. The physical and mechanical properties were found to be better when the compression ratio was 33%: the density increased from 0.33 g/cm3 to 0.58 g/cm3; the surface hardness increased from 33.6 HD to 70.9 HD; the static bending strength increased from 60.4 MPa to 98.7 MPa; and the elastic modulus increased from 6 390 MPa to 11 498 MPa. After 30 days of release, the compression rebound rate was 3.97%. Meanwhile, the micromorphology and heat resistance of the impregnated compressed Chinese fir showed that the PF–montmorillonite impregnation solution entered into the cell cavity and intercellular space of the Chinese fir and formed a good composite, thus improving the water resistance, heat resistance, and physical and mechanical properties.

Study on Impregnation Formula and Process Optimization for Flame Retardant of Chinese Fir

Research on Fire Retardant Performance of Wood with the Compound of Potassium Carbonate and SiO2 Gels

Research On Fire Retardant Performance Of Chinese Fir With The Compound Of Disodium Octaborate Tetrahydrate And Sio2 Gels

Effects of SiO2 Sol on Leachability of Wood Impregnated with Disodium Octaborate Tetrahydrate

Flame-retardancy and Smoke Suppression Characteristics of Bamboo Impregnated with Silicate-Intercalated Calcium Aluminum Hydrotalcates

Use Impregnation and Densification to Improve Mechanical Properties and Combustion Performance of Chinese Fir

Infusing phytate-based biomass flame retardants into the cellulose lumens of Chinese fir wood attains superior flame retardant efficacy

Effect of phosphorus/nitrogen/carbon component ratio in aqueous flame retardant on the fire prevention of wood substrate

Flame retardant modification of poplar wood based on sustainable impregnation solution with high biomass content

Effective strategy for fabricating surface impregnated and unilaterally densified wood with furfuryl alcohol/flame retardants for enhanced mechanical performance and flame retardancy

The Combustion and Mechanical Properties of Guanidine Phosphate-Boron Compound-Silica Sol Composite Flame Retardant on Wooden Structure Building Components

Evaluating the Mechanical and Fire-Resistance Properties of Modified Fast-Growing Chinese Fir Timber with Boric-Phenol-formaldehyde Resin

Progress in Research on Fire Retardant–Treated Wood and Wood-Based Composites: A Chinese Perspective

Construction of a Phytic Acid–Silica System in Wood for Highly Efficient Flame Retardancy and Smoke Suppression

Preparation and Study on Nitrogen- and Phosphorus- Containing Fire Resistant Coatings for Wood by UV-Cured Methods

Evaluation of flammability for bamboo products treated with water-soluble flame retardants

Preparation of Organic-Inorganic Phosphorus-Nitrogen-Based Flame Retardants and Their Application to Plywood

Effect of a biomass based waterborne fire retardant coating on the flame retardancy for wood

Preparation and Application of a Urea–Formaldehyde-Blended Guanidinium Azole–Phytic Acid–Copper Flame-Retardant Resin Coating

Impregnation of phytic acid into the delignified wood to realize excellent flame retardant

Study on Phenol–Formaldehyde Resin–Montmorillonite Impregnation and Compression Modification of Chinese Fir