Formation Mechanism of NaNbO3 Powders During Hydrothermal Synthesis

S. Y. Wu,W. Zhang,X. M. Chen

DOI: https://doi.org/10.1007/s10854-009-9937-9

2009-01-01

Journal of Materials Science Materials in Electronics

Abstract:Hydrothermal synthesis of NaNbO3 fine powders was investigated, and the formation mechanism was revealed. The lowest temperature to form NaNbO3 powders was about 140 °C. An intermediate hexaniobate, Na8Nb6O19·13H2O, was formed first before the precursors were eventually converted to the perovskite phase. The step of dissolving Nb2O5 powders in OH− solution and forming Nb6O19 8− ion was very important to the synthesis of NaNbO3. For [OH−] = 3.0 M, Nb2O5 had the highest yield. There was another dissolvable sodium niobate in the hydrothermal system, which was stable when [OH−] = 1.2 M. The reaction mechanism was in situ transformation. The reaction speed first increased then decreased with [OH−]. High [OH−] is not always favorable in preparing perovskite NaNbO3, and there is an optimum [OH−].