nano-Al_2O_3/Ni+Co gradient composite coating by electrodeposition

LIU Yan,YU Si-rong,REN Lu-quan,HAN Zhi-wu

2009-01-01

Abstract:The metal and nano-ceramic nanocomposite coatings were prepared on gray cast iron surface by electrodeposition method.The nickel and cobalt were used as metal matrix,and the nano-Al2O3 was chosen as secondphase particulates.To avoid bad interface bonding and stress distribution,the gradient composite coating was prepared.Due to the high actively surface of nanoparticles provides an amount of nucleus the morphology of composite coatings was flatter and microstructure was denser than pure nickel and cobalt coatings.The result of line scan content indicated that nano-Al2O3 content distributed gradient.The measure data of microhardness indicated that the microhardness changed in gradient from outer layer to inter layer in coating.The wear experiments indicated that wear-resistance of the composite coating was well than pure nickel cobalt coating evidently.The reason was that nano-Al2O3 caused dispersive strengthening and grain refining.The wear morphologies of composite coating and pure nickel cobalt coating were observed.The results indicate that the composite coating abrasive grooves could be found alongside some cracks which were parallel to the sliding direction,severe plastic deformation could be observed on pure nickel cobalt coating wear surface and the wear mechism was ahension wear.