Abstract:One-dimensional zinc oxide with flower like configuration was synthesized onto a conductor glass substrate (fluorine-doped tin oxide — FTO) at 90°C during 4 and 16h. The zinc oxide formation occurs without any use of pre-seed layer or reactants to increase ionic strength of medium, neither addition of surfactant to act as capping agents for controlling morphology or special treatment on the commercial FTO substrate, making this an efficient and inexpensive procedure. X-ray diffraction analysis evidences a structure composed by single crystal in the wurtzite phase. The flower-like configuration observed by field emission scanning electronic microscopy images was promoted by the interaction between the reactant used to prepare the initial solution with pH adjusted at 10.5. This pH value is found, by titration study (triplicate) and in agreement with many reports in the literature, to promote the powder formation of zinc oxide with flower-like configuration. Tubular ZnO flower-like formation on the FTO was attributed to etching caused by ammonia in high concentration during the hydrothermal synthesis. In addition, our experimental results combined with theoretical ab initio calculation lead us to propose that the formation of tubular flower-like zinc oxide films proceeds in three steps, when prepared by hydrothermal process at different times (at T=90°C).

Fabrication and Characterization of Flower‐Like ZnO by Gemini Surfactant‐Assisted Hydrothermal Process

A Facile Method to Fabricate Superhydrophobic ZnO Nanostructure with Petal Effect

Facile Fabrication of Porous ZnO by a Template Free Method

Morphology Investigation of Hydrothermally Prepared ZnO Micro-Crystals Influenced by Cu2+ Ions

Hydrothermal Preparation of ZnO Nanorods Using Zinc Powder As Precursor and Their Characterization

Assisted-Hydrothermal Synthesis and Characterization of Flower-Like ZnO Nanostructures

Sequential Occurrence of ZnO Nanopaticles, Nanorods, and Nanotips During Hydrothermal Process in a Dilute Aqueous Solution

Synthesis and Characterization of Flower-Like Bundles of ZnO Nanosheets by a Surfactant-Free Hydrothermal Process

A Simple and Novel Low-Temperature Hydrothermal Synthesis of ZnO Nanorods

Synthesis of Flower-Like Zno Nanostructures by an Organic-Free Hydrothermal Process

Zinc oxide flower-like synthesized under hydrothermal conditions

Arrays of ZnO Nanowires Fabricated by a Simple Chemical Solution Route

Photoluminescent Hierarchical Zno Micro‐flower and Its Surface Wettability

Low Temperature Synthesis of Flowerlike ZnO Nanostructures by Cetyltrimethylammonium Bromide-Assisted Hydrothermal Process

Fabrication of ZnO/Al2O3 core–shell nanostructures and crystalline Al2O3 nanotube

Growth of 3-D Flower/Grass-Like Metal Oxide Nanoarchitectures Based on Catalyst-Assisted Oxidation Method

Growth of flower-like ZnO on ZnO nanorod arrays created on zinc substrate through low-temperature hydrothermal synthesis

Preparation and Photoluminescence of ZnO with Nanostructure by Hollow-Cathode Discharge

Hydrothermal Synthesis and Optical Properties of ZnO Nanostructured Films Directly Grown From/on Zinc Substrates

Synthesis of ZnO Nanoflowers and Their Wettabilities and Photocatalytic Properties.

Rapid synthesis of novel flowerlike ZnO structures by thermolysis of zinc acetate