Abstract:One-dimensional zinc oxide with flower like configuration was synthesized onto a conductor glass substrate (fluorine-doped tin oxide — FTO) at 90°C during 4 and 16h. The zinc oxide formation occurs without any use of pre-seed layer or reactants to increase ionic strength of medium, neither addition of surfactant to act as capping agents for controlling morphology or special treatment on the commercial FTO substrate, making this an efficient and inexpensive procedure. X-ray diffraction analysis evidences a structure composed by single crystal in the wurtzite phase. The flower-like configuration observed by field emission scanning electronic microscopy images was promoted by the interaction between the reactant used to prepare the initial solution with pH adjusted at 10.5. This pH value is found, by titration study (triplicate) and in agreement with many reports in the literature, to promote the powder formation of zinc oxide with flower-like configuration. Tubular ZnO flower-like formation on the FTO was attributed to etching caused by ammonia in high concentration during the hydrothermal synthesis. In addition, our experimental results combined with theoretical ab initio calculation lead us to propose that the formation of tubular flower-like zinc oxide films proceeds in three steps, when prepared by hydrothermal process at different times (at T=90°C).

Assisted-Hydrothermal Synthesis and Characterization of Flower-Like ZnO Nanostructures

Conversion of large-scale oriented ZnO rod array into nanotube array under hydrothermal etching condition via one-step synthesis approach

Morphology Investigation of Hydrothermally Prepared ZnO Micro-Crystals Influenced by Cu2+ Ions

A Facile Method to Fabricate Superhydrophobic ZnO Nanostructure with Petal Effect

Self-assembled Flower-Like Hierarchical Spheres and Nanobelts of Manganese Oxide by Hydrothermal Method and Morphology Control of Them

Synthesis of Flower-Like Zno Nanostructures by an Organic-Free Hydrothermal Process

Photoluminescent Hierarchical Zno Micro‐flower and Its Surface Wettability

Hydrothermal Synthesis of Well-Aligned ZnO Nanorod Arrays on Silicon

A Simple and Novel Low-Temperature Hydrothermal Synthesis of ZnO Nanorods

Sequential Occurrence of ZnO Nanopaticles, Nanorods, and Nanotips During Hydrothermal Process in a Dilute Aqueous Solution

Morphology-Controllable synthesis of ZnO nano-/Micro- Structures by a solvothermal process in ethanol solution

Synthesis and Characterization of Flower-Like Bundles of ZnO Nanosheets by a Surfactant-Free Hydrothermal Process

Low Temperature Synthesis of Flowerlike ZnO Nanostructures by Cetyltrimethylammonium Bromide-Assisted Hydrothermal Process

Growth of flower-like ZnO on ZnO nanorod arrays created on zinc substrate through low-temperature hydrothermal synthesis

Hydrothermal Synthesis of ZnO Nanoflowers: Exploring the Relationship between Morphology, Defects, and Photocatalytic Activity

Alkali-dependent Synthesis of Flower-Like ZnO Structures with Enhanced Photocatalytic Activity Via a Facile Hydrothermal Method

Growth of 3-D Flower/Grass-Like Metal Oxide Nanoarchitectures Based on Catalyst-Assisted Oxidation Method

Zinc oxide flower-like synthesized under hydrothermal conditions

Hydrothermal self-assembling of ZnO nanorods into sphere-like superstructures and their optical characteristics

Facile and Controllable Growth of ZnO 1D Nanostructure Arrays on Zn Substrate by Hydrothermal Process

Fabrication and Morphology of ZnO Nanorods Array Prepared from Aqueous Solution under an Assisted Electrical Field