Abstract:Ti(C0.7,N0.3)-Mo2C–Ni cermets are fabricated by powder metallurgy methods. We systematically investigate the microstructure, fracture morphology, crack propagation mechanism, and interface characteristics of Ti(C, N)-based cermets with different Ni binder contents.The increased dissolution of carbides and carbonitrides leads to a large amount of (Mo,Ti)(C,N) solid solution precipitates, which then spontaneously nucleate, resulting in a significant increase in the content of white core-gray rim grains in the cermets with a high binder content. The increased Ni binder largely improves the flexural strength and fracture toughness of the Ti(C,N)-based cermets because of the ductile dispersion toughening. The rim-core interfaces have a superior atomic coherent relationship in all Ti(C,N)-based cermets owing to the small lattice mismatch. The lattice mismatch of the interface between the rim phase and metal binder is remarkably decreased with the increase in the binder content to construct an atomic coherent relationship. Thus, the increased Ni binder promotes atomic ordering at the interface between the ceramic grains and binder and strengthens the grain boundary. The characteristic (111) peak of nickel shifts to a larger angle due to the reduction in the Ni-based solid solution lattice distortion. Therefore, the effect of solid solution strengthening is diminished with the increase in binder content, which results in a decreased binder strength. In the Ti(C,N)-based cermets with low metal binder contents, the fracture of the grain boundary between the ceramic grains and binder is the predominant failure mechanism. The intergranular crack accompanied by crack branching is the main characteristic of crack propagation. A hybrid fracture mode of intergranular and transgranular cracks is observed in the Ti(C,N)-based cermets with a moderate binder content. As the binder content further increases, the plastic yield deformation and subsequent tearing of the metal binder are the main fracture characteristics because of grain boundary strengthening and decreased strength of the binder.

Influence of Molybdenum Content on the Structure and Characteristic of Rim Phase of Ti(C, N)-based Cermets

Influence of Mo addition on microstructure and mechanical properties of Ti(C,N)-based cermets fabricated by in-situ carbothermal reduction of TiO2

Effect of Mo Addition on Microstructure, Magnetic and Mechanical Properties of TiC-TiN-WC-Ni Cermets

Effect of Molybdenum Addition on the Microstructure and Mechanical Properties of Cr3c2-20 Wt. % Ni Cermet

Effect of Mo Content on In-Situ Anisometric Grains Growth and Mechanical Properties of Mo2FeB2-Based Cermets

Effect of Ni Content on the Microstructure, Mechanical Properties and Erosive Wear of Mo2NiB2–Ni Cermets

Fracture Behaviors of Ti(C, N)-based Cermets with Different Contents of Metal Binder

Experimental Investigation and Thermodynamic Analysis of TiC–Fe Cermets with Mo Additions

The Formation of Ni-Mo Alloy Phase in Ticn-Based Cermets

Influence of TaC content on microstructure and mechanical performance of Ti(C,N)-based cermets fabricated by mechanical activation and subsequent in situ carbothermal reduction

Effect of C content on the surface gradient structure of (Ti, Mo)(C, N) and Ti(C, N)-based cermets

Microstructure and Properties of Ti(C,N)-Based Cermets with AlxCoCrFeNiTi Binder

Fabrication, microstructure evolution, and mechanical properties of Ti(C,N)-HfN-WC-Ni-Mo cermets

Effect of Y2O3 Addition on the Microstructure and Mechanical Properties of TiCN-based Cermets

Improvement of high temperature oxidation behavior of Cr3C2-20 wt % Ni cermets by adding 1 wt % Mo

Influence of WC content on microstructure and mechanical properties of Mo2FeB2-based cermets fabricated by multi-step sintering

Evolution of microstructure and interfacial characteristics of complete solid-solution Ti(C,N)-based cermets fabricated by mechanical activation and subsequent in situ carbothermal reduction

Effect of Cr2C3 addition on microstructure and mechanical properties of Ti(CN)-based cermets

Tuning microstructure for superb mechanical properties in a Ti(C,N)-(WMoTaNbTi)C-Ni/Co cermets via change sintering temperature

Improvement of High Temperature Wear Behavior of In-Situ Cr3C2-20 Wt. % Ni Cermet by Adding Mo

Sintering Mechanism, Microstructure Evolution and Nanomechanical Properties of Cr-added Mo2FeB2 Based Cermets