Abstract:Ti-6.5Al-2Zr-1Mo-1V/TiB metal matrix composites with 3 wt.% of TiB2 were obtained using vacuum arc melting and spark plasma sintering methods and compared with an unreinforced Ti-6.5Al-2Zr-1Mo-1V alloy. The microstructures of the unreinforced Ti6.5Al-2Zr-1Mo-1V alloy in the as-cast and as-sintered conditions were quite typical and consisted of colonies of α-lamellae embedded in the β matrix. The microstructure of the as-cast Ti-6.5Al-2Zr-1Mo-1V/TiB composite composed of TiB fibers randomly distributed within the two-phase α/β matrix, while the as-sintered composite had a network-like microstructure, in which areas of the two-phase α/β matrix were delineated by walls of TiB fibers. At room temperature, the yield strength of the as-cast and as-sintered Ti-6.5Al-2Zr-1Mo-1V alloy were 800 and 915 MPa, respectively, with a plasticity of 18% in both conditions. The addition of TiB fibers contributed to a ~40 and 50% strength increment, with values of 1100 and 1370 MPa for the as-cast and as-sintered composites, respectively. In the as-sintered composite, the strengthening effect reduced at 400 °C and almost disappeared at elevated temperatures of 800–950 °C. The as-cast composite showed much higher strength during warm and hot deformation—at 800–950 °C, the yield strength of the as-cast composite was 50% higher compared to the Ti-6.5Al-2Zr-1Mo-1V unreinforced alloy. A higher rate and degree of globularization were established for the as-cast composite compared to the unreinforced alloy. For the as-sintered composite, a noticeably lower rate and degree of globularization was shown. During hot compression of the as-cast composite, TiB fibers reoriented towards the metal flow direction, while the network microstructure formed in the as-sintered composite transformed into clusters of borides unevenly distributed within the matrix. Based on the obtained results, the apparent activation energy of plastic deformation was calculated, and the operating deformation mechanisms were discussed both for the as-cast and as-sintered composites. The Arrhenius flow stress model and the dynamic material model were used to evaluate the deformation behavior of composites beyond the experimentally studied temperatures and strain rates.

Viscosity of TiB_2/Al Composite Molt

High Temperature Tensile Properties of in Situ TiBw/Ti6Al4V Composites with a Novel Network Reinforcement Architecture

PREPARATION AND PROPERTIES OF TiB2/TiAl COMPOSITE SHEETS WITH LAYERED STRUCTURE

Effect of TiB2 particles on thermal deformation behavior and mechanical properties of aluminum alloy

High fatigue performance and microscopic mechanisms of in-situ TiB 2 /7050Al composite at different temperatures

Microstructure and Mechanical Properties of TiB2-Al2O3 Composites

A physically-based model for elevated temperature strength prediction of (TiBw + (Ti, Zr) 5 Si 3 )/Ti-6.5Al-2Zr-1Mo-1V composite

Influence of TiB_2 Particles on the Thermal Stability of Cu_(47)Zr_(40)Al_(13) Bulk Amorphous Alloy Composites

Microstructural evolution and hydrogen content and their effect on properties of TiB 2 /Al-Li-X composites with different Li contents

Study on microstructure and properties of TiBw/Ti-V-Al light weight high temperature shape memory composite

Effect of cooling rate on solidification microstructure and mechanical properties of TiB2-containing TiAl alloy

Microstructure and mechanical properties of TiB 2 -Al 2 O 3 composites

Hot Deformation Behavior and Microstructural Evolution of a TiB2/Al-Zn-Mg-Cu-Zr Composite

Structure and Property of Metal Melt III—Relationship Between Kinematic Viscosity and Size of Atomic Clusters

Micro-Mechanism For The Evolution Of Viscosity Versus Temperature In Magnesium-Aluminum Alloy Melts

Relationship Between Liquid Structure and Property Ⅱ—— Kinematic Viscosity of Mg-9Al Melt and Its Relationship with the Microstructure

Microstructures and mechanical properties of hot indirect extruded in situ (TiB + TiC)/Ti6Al4V composites: Effect of extrusion temperature

Microstructure evolution, deformation behavior and manufacture design of TiAl matrix composites reinforced with in-situ borides precipitation

Dynamic behavior and fracture mode of TiAl intermetallics with different microstructures at elevated temperatures

Microstructure Evolution and Mechanical Behavior of TiB-Reinforced Ti-6.5Al-2Zr-1Mo-1V Matrix Composites Obtained by Vacuum Arc Melting and Spark Plasma Sintering

High temperature performance of TiB/(Ti-6.5Al-2Zr-1Mo-1V-0.5Si) composites affected by the TiB architecture