Theoretical analysis of flexural performance of plain concrete composite beams strengthened with ultrahigh toughness cementitious composite

Xiufang Zhang,Xu Shilang,Hedong Li

2010-01-01

Abstract:A theoretical investigation on the flexural performance of UHTCC/concrete composite beams is presented. The contribution of the tension softening cohesive force at the crack of concrete to the load-carrying capacity of the composite beams was not taken into account. Four-point bending experimental results of three sets of UHTCC/Concrete composite beams were employed to validate the theoretical analysis. A parametric study was carried out, including parameters such as the UHTCC layer thickness, the compressive strength of concrete as well as the tension control parameters of UHTCC, to get a clear understanding of the degree of the influence of various parameters on the flexural performance and the minimum UHTCC layer thickness of the composite beams. The results revealed that (1) the depths of composite beams did not influence the ratio of the minimum thickness of UHTCC layer to depth; (2) when beam size and UHTCC are identical, the minimum thickness of UHTCC and the ultimate flexural capacity of the beams in compression failure mode increased as the compressive strength of concrete increased; and (3) when the size and the concrete are identical, the stiffness after cracking and the tensile strength of UHTCC more significantly affected the minimum depth of UHTCC layer. The curves of flexural load-carrying capacity vs. tensile strain at the bottom of the beams were not affected by the tensile strain of UHTCC, but the flexural load-carrying capacity of the beams increased with increases in first cracking tensile strength and ultimate tensile strength.