Synthesis of Fluorinated Emulsifier-Free Polyacrylate Emulsion in the Presence of Polymerizable Emulsifier
肖新颜,王叶,万彩霞
DOI: https://doi.org/10.3321/j.issn:1000-565X.2009.09.026
2009-01-01
Abstract:Fluorinated emulsifier-free polyacrylate emulsion with a core-shell structure was synthesized via the pre-emulsified seed emulsion polymerization,with methyl methacrylate(MMA),butyl acrylate(BA) and hexafluorobutyl methacrylate(HFMA) as the main monomers,and with ammonium allyloxtmethylate nonylphenol ethoxylates sulfate(DNS-86) as the polymerizable emulsifier.Then,the influences of the dosages of DNS-86 and HFMA on the electrolyte stability of the emulsifier-free emulsion and on the water resistance of the film were discussed.Moreover,the emulsion and the film were characterized by means of FT-IR,TEM,DSC,contact angle method and TG.The results show that,as compared with the traditional complex emulsifier OP-10/SDS,polymerizable emulsifier DNS-86 may result in stronger electrolyte stability and water resistance in the polymerization with 2.2% DNS-86 and 8% HFMA,that HFMA effectively participates the emulsion copolymerization,that there exists a clear core-shell structure in emulsion particles,that the emulsifier-free emulsion film is of two glass transition temperatures,namely 261.11 and 300.48 K,which respectively correspond to the core-phase and the shell-phase copolymers,and that,at a HFMA dosage of 8%,the water contact angle of the film-air interface reaches 94.1° and the decomposition temperature of the emulsifier-free emulsion film is 48 K higher than that of the traditional polyacrylate emulsion film,showing a greatly-improved hydrophobic property and thermal stability of the film.