Abstract:Fluoropolymer films have so low surface energy that they have good special surface properties, such as water-resistant, oil-resistant and self-cleaning properties. Nowdays, surface properties of polyacrylates can be modified by introducing fluorine-containing groups to polymer chains. The acrylate copolymer emulsion containing fluorine was prepared, with fluoromoner ( Zonyl TM), butyl acrylate ( BA), methyl methylacrylate (MMA) as monomers, sodium dodocyl sulfonate ( SDS) as emulsifier. The solid content of copolymer emulsion was about 25wt%. The kinetics of emulsion copolymerization was studied by the weight method. The effects of the concentration of emulsifier, initiator, monomer and polymerization temperature on polymerization rate (R-p) were investigated in detail. The results showed that R-p proportional to [SDS](0.28), R-p proportional to [I](0.98). The apparent activation energy was 50.756 kJ.mol(-1). The copolymer emulsions had no change after stored at room temperature for 72 h, at 60degreesC for 48 h and at -5degreesC for 24 h respectively. The centrifugal stability of emulsions was characterized at 12000 r/min for 120 min. The sedimentation ratios showed that the centrifugal stability of emulsions increased with increasing the amount of emulsifier, while decreased with increasing the amounts of initiator and fluoromonomer respectively. The latex films could be dissolved in THF and toluene, while could be swelled in methanol and ethanol. The water absorption of latex films decreased with increasing the amount of fluoromonomer. The surface property of films was determined by Wilhelmy method. The contact angles for latex films to water increased apparently by introducing fluorine-containing groups, above 100degrees. This result showed the water-resistant property of copolymer latex films containing fluorine was improved.

Synthesis and Properties of Soap-Free Fluorinated Acrylate Copolymer Emulsion via Miniemulsion Polymerization

Properties and Characterization of Novel Cationic Polyacrylate Latex Containing Fluorine and Silicon Prepared with Soap-Free Emulsion Polymerization

Synthesis of Fluorinated Acrylate Emulsifier-Free Emulsion Using Polymerizable Emulsifier and Its Properties

Study on Synthesis of Fluorinated Acrylic Copolymer Emulsion and Properties of Films

Emulsion Copolymerization of Fluorinated Acrylate in the Presence of a Polymerizable Emulsifier

Synthesis of Fluorinated Emulsifier-Free Polyacrylate Emulsion in the Presence of Polymerizable Emulsifier

Synthesis of Fluorine-containing Acrylate Copolymer Emulsion

Synthesis and Characterization of Fluorinated Acrylate Emulsion with Core-Shell Structure

Synthesis and Properties of the FA/LMA/MMA Copolymer Emulsion

The Study of the Acrylate Copolymer Emulsion Containing Fluorine

Synthesis and Characterization of Fluorine-containing Polyacrylate Emulsion with Core-Shell Structure

Hydrophobicity of Polyacrylate Emulsion Film Enhanced by Introduction of Nano-SiO₂ and Fluorine

Synthesis of Nano-silica/Fluorinated Polyacrylate Composite Emulsions Via Miniemulsion Polymerization and Study on Its Properties

Stability of Emulsion Polymerization of New Fluorinated Acrylate Emulsion and Its Characterization

Preparation and Surface Property of Cationic Emulsifier-Free Fluorinated Polyacrylates

Synthesis and Performances of Core-Shell Type Styrene-Acrylate Emulsion with Organic-Fluorine and Organic-Silicon

Synthesis and Properties of Nano-SiO2-Perfluoroalkyl Acrylate Modified Acrylate Emulsion via In-Situ Polymerization

Study on Emulsion Polymerization of Fluorinated Acrylate and Its Application

Preparation and Characterization of Soap-Free Fluorine-Containing Acrylate Latex

Synthesis and Properties of Novel Fluorinated Cationic Polymer Latex

Synthesis and characterization of fluorinated polyacrylate latex emulsified with novel surfactants