Abstract:TiO2-coated (Na0.85K0.15)(0.5)Bi0.5TiO3 (NKBT) composite films with thicknesses of 250 nm and 650 nm are synthesized on Pt(111)/Ti/SiO2/Si using an aqueous sol-gel method. X-ray diffraction (XRD) in omega-scan and psi-scan modes is performed to study the crystal orientation of the films. The electrical properties of the TiO2-coated NKBT composite films are investigated over a temperature range from -150 degrees C to 150 degrees C. Compared to films without the TiO2 layer, the TiO2-coated NKBT films exhibit enhanced electrical properties, higher temperature stability, and better endurance performance, which can be ascribed to the combined effects of the highly (100)-preferred orientation and improved degree of crystallization. The composite film in which TiO2 layers are attached on both sides of the 650 nm-thick NKBT film demonstrates the best ferroelectric performance with the highest remnant polarization (P-r) of 24.2( +/- 1.2) mu C/cm(2) under 750 kV/cm, the best piezoelectric performance with the highest effective piezoelectric constant (d(33)*) of 82( +/- 4) pm/V, and the best electric performance with the lowest leakage current density of 4.5 x 10(-6)( +/- 0.4 x 10(-6)) A/cm(2) at 20 V. Piezoresponse force microscopy (PFM) further confirms the enhanced ferroelectricity and domain switching of the TiO2 -coated composite films on a microscopic scale. In addition, the P-r values of the films increase gradually as the temperature decreases from 150 degrees C to-150 degrees C, while the d(33)* values exhibit the opposite trend, which is mainly attributed to the suppressed mobility of the domain walls at low temperatures.

Structure and Electrical Properties of Trilayered BaTiO3/(Na0.5Bi0.5)TiO3–BaTiO3/BaTiO3 Thin Films Deposited on Si Substrate

Ferroelectric and pyroelectric properties of (Na0.5Bi0.5)TiO3–BaTiO3 based trilayered thin films

Preparation and ferroelectric properties of (Na0.5Bi0.5)0.94Ba0.06TiO3 thin films deposited on Pt electrodes using LaNiO3 as buffer layer

Dielectric and Ferroelectric Properties of Highly (100)-Oriented (na0.5bi0.5)0.94ba0.06tio3 Thin Films Grown on LaNiO3/γ-Al2O3/Si Substrates by Chemical Solution Deposition

Dielectric and piezoelectric properties of highly (100)-oriented BaTiO3 thin film grown on a Pt/TiOx/SiO2/Si substrate using LaNiO3 as a buffer layer

Structure and Electrical Properties of Bi3.15nd0.85ti3o12 Ferroelectric Thin Films

Dielectric and piezoelectric properties of highly (1 0 0)-oriented BaTiO3 thin film grown on a Pt/TiOx/SiO2/Si substrate using LaNiO3 as a buffer layer

Enhancement of Piezoelectric and Ferroelectric Performances in (na0.85k0.15)0.5bi0.5tio3 Films with BaTiO3 Interlayers

Microstructure and Electric Properties of (na0.85k0.15)(0.5)bi0.5tio3 Composited Films with Alternative Tio2 Layers

Dielectric and tunable properties of highly (110)-oriented (Ba 0.65 Sr 0.35 )TiO 3 thin films deposited on Pt/LaNiO 3 /SiO 2 /Si substrates

Structural, Ferroelectric, Dielectric, And Magnetic Properties Of Bifeo3/Bi3.15nd0.85ti3o12 Multilayer Films Derived By Chemical Solution Deposition

Preparation and Properties of Bi 4 − x Nd x Ti 3 O 12 Thin Films by Chemical Solution Deposition

Microstructure And Ferroelectric Properties Of Sol-Gel Derived Bi3.15nd0.85ti3o12 Thin Films On Pt/Ti/Sio2/Si(100)

Electrical Properties of Chemical-Solution-derived Bi3.54Nd0.46Ti3O12 Ferroelectric Thin Films

Preparation and Properties of Bi4 ? Xndxti3o12 Thin Films by Chemical Solution Deposition

Growth Orientation-Related Enhancement of Electrical Properties in (Na0.85k0.15)0.5bi0.5tio3-Based Composite Films

Composition-Dependent Electrical Characteristics And Interface Microstructures Of Solution-Derived Nd-Substituted Bi4ti3o12 Thin Films On Pt Electrodes

Chemically Deposited (100)-Oriented BaTiO3 Films with Highly Concentrated Solution Using High Crystallinity BaTiO3 As a Buffer Layer

Electrical Properties of (100)-Predominant BaTiO3 Films Derived from Alkoxide Solutions of Two Concentrations

Chemical Solution Deposition And Electrical Properties Of (100)-Predominant Batio3 Thicker Films

Enhanced Dielectric and Piezoelectric Properties in Lead-Free Bi0.5Na0.5TiO3–BaTiO3–SrTiO3 Thin Films with Seed Layer