Abstract:IPP hollow-fiber microporous membranes were prepared via thermally induced phase separation (TIPS) with cosolvent di-n-butyl phthalate (DBP) and dioctyl phthalate (DOP). The DOP mass fraction in co-solvent (α) and iPP mass fraction in a casting solution (β) were worked as the variables in the spinning process. With increasing α, the TIPS of the polymer solution changes to only polymer crystallization from liquid–liquid phase separation with subsequent polymer crystallization. Accordingly, the morphology of the resulting membrane changes from a typical cellular structure to a mixed structure, which is basically cellular but with particulate boundaries, and then a typical particulate structure. As a result, permeability of the membrane increases sharply and mechanical properties of the membrane decrease obviously. Therefore, the iPP hollow-fiber microporous membrane with higher permeability and higher mechanical properties must exhibit a mixed membrane morphology in which liquid–liquid phase separation precedes polymer crystallization. However, by varying β, both the phase separation pattern of the iPP solution and types of the resulting membrane structure cannot be changed. The permeability of resulting membrane decreases with increasing β, but the mechanical properties increase with increasing β. It is noted also that those iPP hollow-fiber microporous membranes are apt to possess a narrow pore size distribution. It is indicated that by choosing proper α and β, the membrane morphology can be an open cellular pore structure; moreover, the resulting membrane exhibits both higher permeability and higher mechanical properties. It is suggested that for a crystalline polymer such as iPP, by a proper approach, adjusting the competition between liquid–liquid phase separation and polymer crystallization is the key to creating the membrane with an interconnecting pore structure and good performance.

Cryogenic Induced Phase Separation of Chitosan Solution

Supercritical Carbon Dioxide Extraction in Membrane Formation by Thermally Induced Phase Separation

Preparation of High Density Polyethylene/polyethylene- Block -Poly(ethylene Glycol) Copolymer Blend Porous Membranes Via Thermally Induced Phase Separation Process and Their Properties

Solid-liquid phase separation of poly-4-methyl-1 pentene/diluent system via thermally induced phase separation

Preparation of porous membrane by combined use of thermally and chemical reaction-introduced nonsolvent-induced phase separations

Preparation of Poly(4-methyl-1-pentene) Membranes by Low-Temperature Thermally Induced Phase Separation

Preparation and Characterization of Cellulose Triacetate Membranes Via Thermally Induced Phase Separation

Fabrication of chitosan membranes via aqueous phase separation: Comparing the use of acidic and alkaline dope solutions

Preparation, Structure and Crystallinity of Chitosan Nano-Fibers by a Solid–liquid Phase Separation Technique

Preparation of Polysulfone Membranes Using Ionic Liquid [c(16)mim][scn] As A Pore-Former and Plasticizer

Preparation and Characterization of Microporous PVDF Membrane by Thermally Induced Phase Separation from a Ternary Polymer/solvent/non-Solvent System

Preparation of Porous Poly(ether Ether Ketone) Membranes Via Thermally Induced Phase Separation

Polar Polymer Membranes Via Thermally Induced Phase Separation Using A Universal Crystallizable Diluent

Preparation of Ethylene Chlorotrifluoroethylene Co-polymer Membranes Via Thermally Induced Phase Separation

Development of Polymer Microporous Membranes Via Thermally Induced Phase Separation

Formation of Hydrophilic Ethylene-Acrylic Acid Copolymer Microporous Membranes Via Thermally Induced Phase Separation

Preparation of Ipp Hollow-Fiber Microporous Membranes Via Thermally Induced Phase Separation with Co-Solvents of DBP and DOP

Preparation of 4-methyl-1-pentene membranes via non-solvent induced phase separation (NIPS)

Thermally Induced Phase Separation of Poly(vinylidene Fluoride)/diluent Systems: Optical Microscope and Infrared Spectroscopy Studies

Thermophysical Properties of Polycaprolactone/chitosan Blend Membranes

The Effect of Diluent Mixture with Upper Critical Solution Temperature on Membrane Formation Process, Microstructure, and Performance of PVDF Hollow Fiber Membrane by TIPS Process