Abstract:The reduction behavior of a sintered NiO/YSZ anode used for intermediate temperature solid oxide fuel cells was studied by hydrogen temperature-programmed reduction (H-2-TPR). The reduction process of the NiO/YSZ anode in the cell was in situ monitored by open circuit voltage (OCV) and electrochemical impedance spectroscopy (EIS). H-2-TPR results show that the higher sintering temperature of the NiO/YSZ anode results in a slower reduction of NiO to metallic Ni. However, when the sintering temperature is elevated to 1500 degrees C, the reduction of sintered NiO/YSZ anode powder instead becomes easier. The higher NiO content in the anode leads to the more rapid reduction of the corresponding anode powder. The above H2-TPR results can be attributed to the combined effects of the growth up of NiO particles and the interface separation between NiO and YSZ caused by the anode sintering. The variation of OCVs reveals that for the cells, the anode with higher NiO content has a slower reduction process, which can be ascribed to the retarding effect of excessive H2O produced during the initial reduction period. It was found from the EIS results that the 50% NiO/YSZ anode has a most stable reduction process, whereas for the cells with 30 % and 70 % NiO/YSZ anodes, both the polarization resistances gradually increase after experiencing an initial decrease for a short period. The cell polarization resistance with 30 % NiO/YSZ anode keeps no change any more after reduction for 600 min, whereas the cell polarization resistance with 70 % NiO/YSZ anode increases continuously.

Redox behavior of supported Pd particles and its effect on oxygen reduction reaction in intermediate temperature solid oxide fuel cells

Pd-YSZ composite cathodes for oxygen reduction reaction of intermediate-temperature solid oxide fuel cells

Electrochemical Performance and Stability of Nano-Structured Co/PdO-co-impregnated Y2O3 Stabilized ZrO2 Cathode for Intermediate Temperature Solid Oxide Fuel Cells

Novel Nano-Structured Pd+yttrium Doped ZrO2 Cathodes for Intermediate Temperature Solid Oxide Fuel Cells

Comparative Study of Pd and PdO As Cathodes for Oxygen Reduction Reaction in Intermediate Temperature Solid Oxide Fuel Cells

Mn-Stabilised Microstructure and Performance of Pd-impregnated YSZ Cathode for Intermediate Temperature Solid Oxide Fuel Cells

PdO/ZrO2 engineered (La0.8Sr0.2)0.95MnO3-δ-(Y2O3)0.08(ZrO2)0.92 cathode for use in intermediate temperature solid oxide fuel cells

Performance and Durability of an Anode-Supported Solid Oxide Fuel Cell with a PdO/ZrO2 Engineered (La0.8sr0.2)0.95mno3-Δ-(y2o3)0.08(zro2)0.92 Composite Cathode

Effect of Reduction Temperature on the Electrochemical Properties of a Ni/YSZ Anode-Supported Solid Oxide Fuel Cell

Nano-structured (La, Sr)(Co, Fe)O3 + YSZ composite cathodes for intermediate temperature solid oxide fuel cells

High performance solid oxide fuel cells with electrocatalytically enhanced (La, Sr)MnO3 cathodes

Promoted electrochemical performance of intermediate temperature solid oxide fuel cells with Pd 0.95 Mn 0.05 O-infiltrated (La 0.8 Sr 0.2 ) 0.95 MnO 3−δ –Y 0.16 Zr 0.84 O 2 composite cathodes

The Reduction Process of a NiO/YSZ Anode for Intermediate Temperature Solid Oxide Fuel Cells

Electroless Deposition of Co(Mn)/Pd-decorator into Y2O3-stabilized ZrO2 Scaffold As Cathodes for Solid Oxide Fuel Cells

Effects of Initial Reduction Temperature on the Microstructures and Performances of Ni/YSZ Anodes for Solid Oxide Fuel Cells

Electrochemical Performance and Stability of Sr-doped LaMnO 3 -Infiltrated Yttria Stabilized Zirconia Oxygen Electrode for Reversible Solid Oxide Fuel Cells

Composition optimization of samarium strontium manganite-yttria stabilized zirconia cathode for high performance intermediate temperature solid oxide fuel cells

Effect of Pd doping on the activity and stability of directly assembled La0.95Co0.19Fe0.76Pd0.05O3-δ cathodes of solid oxide fuel cells

Electrochemical Stability of La0.6Sr0.4Co0.2Fe0.8O3−δ-infiltrated YSZ Oxygen Electrode for Reversible Solid Oxide Fuel Cells

Improved electrochemical performance and durability of butane‐operating low‐temperature solid oxide fuel cell through palladium infiltration

Electrochemical performance and redox stability of solid oxide fuel cells supported on dual-layered anodes of Ni-YSZ cermet and Ni–Fe alloy