Performance and Electrochemical Behavior of LSM Based Fuel Electrode Materials Under High Temperature Electrolysis Conditions
Vaibhav Vibhu,Izaak Vinke,Rudiger-A Eichel,L.G.J. (Bert) de Haart
DOI: https://doi.org/10.1149/11106.1401ecst
2023-05-19
ECS Transactions
Abstract:Ni-YSZ is known as the state-of-the-art fuel electrode material for solid oxide cells. However, this conventional fuel electrode experiences severe degradation due to Ni- agglomeration and migration away from the electrolyte. Therefore, to avoid such issues, we have considered Ni free electrodes i.e. La 0.6 Sr 0.4 MnO 3 (LSM) based perovskite oxides as fuel electrode. Under reducing atmosphere, the LSM perovskite phase transforms into a Ruddlesden-Popper (La 0.6 Sr 0.4 ) 2 MnO 4±δ phase. In addition to pure LSM fuel electrode, we have also investigated the performance of LSM+YSZ (50:50 wt %) and LSM+GDC (50:50 wt %) composite electrodes. The electrolyte-supported single cells were prepared using 8YSZ electrolyte supports, and in all cases, LSM+YSZ/LSM oxygen electrodes were used. The current-voltage characteristics show good performance for LSM and LSM+GDC fuel electrode containing single cells. However, a lower performance is observed for LSM+YSZ fuel electrode containing single cell. For instance, a current density of 997, 1025, and 511 mA.cm -2 at 1.5 V, are obtained for LSM, LSM+GDC, and LSM+YSZ fuel electrode containing single cells respectively, with 50% N 2 and 50% H 2 O feed gas mixture.