Abstract:Mesoporous titania-silica (TiO2-SiO2) composites have been directly synthesized through a hydrothermal method in weak acidic conditions by using TiCl3 solution as a titanium source and triblock copolymer P123 (EO20PO70EO20) as a template with the assistance of zinc acetate. Characterizations by XRD, TEM, and N-2 sorption measurements show that highly ordered mesostructured TiO2-SiO2 with the BET specific area of 882 m(2)/g was obtained with the Ti/Si molar ratio of 0.1. Morphology of the composites can be controlled by the incorporation of different amounts of titanium species. Highly curved shapes such as winding, wormlike, and wheat grain-like particles were obtained by this direct synthetic method. Acidity and zinc acetate concentration can also affect the morphology of the composites. UV-vis, FTIR and Si-29 MAS NMR results display that titanium species exist both in the framework and extra-framework of the mesoporous SiO2. Wide angle XRD, Raman, and HRSEM results show that the outer surface of the SiO2 (probably Ti-doped) is decorated by round anatase nanocrystallites (probably Si-doped), whereas X-ray mapping results reveal that titanium species are highly dispersed on the final mesoporous composites. The formation mechanism of the mesophase was discussed based on characterization results. Photocatalytic results show that the TiO2-SiO2 composites prepared in this way have high catalytic activity in the photodegradation of isopropanol due to both framework and surface titanium species.

Synthesis of Ordered Mesoporous TiO<sub>2</sub> by Hydrolysis Condensation with Block Copolymer P123 as Template

Synthesis of Ordered Mesoporous TiO<sub>2</sub> on a Composite Surfactant Template

Synthesis and Characterization of Mesoporous TiO2 with Wormhole-Like Framework Structure

Synthesis of Well-Ordered Mesoporous Titania with Tunable Phase Content and High Photoactivity

Hydrothermal Synthesis and Morphological Evolution of Mesoporous Titania−Silica

Synthesis of easily shaped ordered mesoporous titanium-containing silica

Preparation Nano TiO2 Mesoporous Material by Soft Template

Controlled synthesis of ordered mesoporous C-TiO2 nanocomposites with crystalline titania frameworks from organic-inorganic-amphiphilic coassembly

Synthesis of ordered mesoporous bifunctional TiO2–SiO2–polymer nanocomposites

Synthesis of Mesoporous TiO2 with a Crystalline Framework

Synthesis of semicrystallized mesoporous TiO2 thin films using triblock copolymer templates

Preparation and photocatalytic activity of mesoporous TiO2 derived from hydrolysis condensation with TX-100 as template

Synthesis and characterization of mesoporous titanium dioxide

Template-free Hydrothermal Synthesis of Macroporous TiO2 Microspheres on a Large Scale

Synthesis of Mesoporous Thin Tio2 Films with Hexagonal Pore Structures Using Triblock Copolymer Templates

Controlled Synthesis of Mesoporous Silicas Mcm-48 and Mcm-41 by Using Mixed Templates

Synthesis of ordered mesoporous crystalline carbon-anatase composites with high titania contents.

Preparation Of Nanocrystalline Titania Mesoporous Films By Template Assembled Method

Synthesis of Mesoporous Titania with High Photocatalytic Activity by Nanocrystalline Particle Assembly

Preparation and hydrophilicity of mesoporous TiO2 thin films

Ordered Mesoporous Silicate Materials from a Template of Triblock Copolymer (I): Size Control and Characterization of Powder