Abstract:The microstructure and hydrogen storage properties of Ti10+xV80-xFe6Zr4 (x = 0, 5, 10, 15) alloys have been studied. XRD and SEM analyses show that all alloys consist of a BCC main phase and a small fraction of C14 Laves secondary phase, in which the latter precipitates along the grain boundary of the former becoming network structure. With increasing Ti content in the alloy, the lattice parameter and cell volume of the BCC main phase of the alloy increase. The chemical composition of each phase is analysed by EDS, from which the lattice parameters of BCC phase have a good linear relationship with their average atomic radii. All bulk alloys have good activation behaviors and hydriding kinetics. With the increase of Ti content, the incubation time for activation decreases first and then increases under an initial hydrogen pressure of 4 MPa at 298 K. The incubation time of Ti15V75Fe6Zr4 alloy is only 12 s. It is one of the shortest incubation time in V-based solid solution alloys as far as we know, which may be related to the existence of C14 Laves phase. All the alloys have relatively high hydrogen absorption capacities of above 3 wt%, which increase first and then decrease as the Ti content increases, achieving the maximum capacity of 3.61 wt% at x = 10 at 298 K. With increasing x, the equilibrium plateau pressure of dehydrogenation of the samples at 353 K decreases owing to the expansion of unit cell of main phase, which is far below 0.1 MPa for x = 10 and 15. The maximum desorption capacity of 1.94 wt% (desorbed to 0.001 MPa) is obtained at x = 5, compared to that of 1.6 wt% (desorbed to 0.1 MPa) achieved at x = 0.

Hydrogen absorption performance of Ti?V-based alloys surface modified by carbon nanotubes

Experimental and Theoretical Investigation on the Enhanced Hydrogen Storage Performance of Ti–Cr–Mn–Fe-Based Alloys Modified by Nb Substitution

Synergism of Nano ZnO for Improvement of Hydrogen Absorption Performance of Ti–V-based Alloys

Hydrogen storage properties of V+TiFe0.85Mn0.15 multi-phase alloys

Hydrogen storage performance of quenched Ti–V-based alloy

Hydrogen Storage Properties of Ti-Cr-Mn-M (M=V, Fe, Ni, Cu) Alloys

Microstructure and hydrogen storage properties of Ti10+xV80-xFe6Zr4 (x=0~15) alloys

Studies of hydrogen storage properties and absorption-desorption mechanism of FeTi1.3(Mm)y alloy

Microstructure and hydrogen storage properties of Ti1.0VxMn2-x(x=0.6-1.6) alloys

Effect of Carbon on Hydrogen Storage Performances of TiMn1.25Cr0.25 Alloy

Hydrogen storage capabilities of the alloys Fe 0.85Mn 0.15Ti 0.9M 0.1 (M=Zr, V, Ca)

Microstructures and Hydrogen Storage Properties of Ti10V83-xFe6ZrMnx Alloys

Microstructure And Hydrogen Storage Properties Of La1.8ca0.2mg14ni3 + X% Ti Composites

Hydrogen Storage Properties and Crystal Structure of Ti-Cr Based Alloys

Microstructure and Electrochemical Properties of V_(2.1)TiNi_(0.4)Zr_(0.06)Cu_(0.03)M_(0.10)(M=Cr, Co, Fe, Nb, Ta) Hydrogen Storage Alloys

Effect of Carbon Addition on Activation and Hydrogen Sorption Characteristics of TiMn1.25Cr0.25 Alloy

Preparation and Electrochemical Hydrogen Storage Properties of MWCNTs-doped Ti49Zr26Ni25 Alloy Containing Quasicrystal Phase

Electrochemical Hydrogen Storage in Ti–V-based Alloys Surface-Modified with Carbon Nanoparticles

Enhancement of Hydrogen Storage Capacity of Ti–V–Cr–Mn BCC Phase Alloys

Activation and Hydrogen Absorption-Desorption Properties of Timn0.85cr0.35v0.3 Alloy

Effect of Annealing on Phase Structure and Performance of TiMn-based Hydrogen Storage Alloy