Abstract:Sulphonated waterborne polyurethane emulsions with 50% solid-content were successfully synthesized by using poly(1,4-butanediol adipate)diol (PBA), isophorone diisocyanate (IPDI) and hexamethylene diisocyanate (HDI) as the main raw materials, N-(2-aminoethyl)-amino ethane sulphonated sodium as hydrophilic chain extender, and HDI trimer (HT) as a modifier. The effects of the feeding method and the amount of HDI trimer on the latex particle size and distribution, Zeta potential and viscosity of waterborne polyurethane emulsions, and the water resistance, crystallinity and mechanical properties of the cast films of synthesized polyurethane were studied respectively by Malvern laser particle size analyzer, Brookfield viscometer, universal tensile machine, Fourier transform infrared spectroscopy (FT-IR), nuclear magnetic resonance (1H-NMR), X-ray diffraction analysis (XRD), differential scanning calorimetry analysis (DSC) and transmission electron microscopy (TEM). The results show that, with the increase of the amount of HDI trimer, the viscosity of waterborne polyurethane emulsion decreases, the average particle size and its distribution of latex particles increase, and the tensile strength and elongation at break of the cast films are increased firstly and then decreased. The introduction of the HDI trimer into the polyurethane chain destroys the arrangement regularity of the polyurethane soft segment, which results in a slightly lower film crystallinity. When the ratio of HDI trimer to IPDI is 1:3 (mass ratio), the synthesized polyurethane shows excellent performance, which has the emulsion particle size of 199.3 nm, Zeta potential of-42.7 mV, the film water absorption of 3.8%and the film relative crystallinity of 50.62%.

Synthesis and Application of Sodium 1,4-Dihydroxybutane-2-Sulfonate in Synthesis of Polyurethane Ionomer Containing Sulfonate

Synthesis, Characterization and Application of Novel Hydroxyl Sulfonate Monomer-2,2-Bis(hydroxymethyl) Butyric Propyl -3'-Sodium Sulfonate

Distribution of Hydrophilic Monomer Units and Its Effect on the Property of the Water Dispersion of Polyurethaneurea Anionomer

Synthesis and characterization of polyurethane dispersions based on diaminocarboxylate

Synthesis and characterization of polyurethane anionomers

Synthesis and Characterization of Polydioxolane Polyurethane Ionomer

Syntheses of poly(ethylene oxide) polyurethane ionomers

Synthesis and Characterization of Anionic/non-Ionic Type High Solid Content Polyurethane Dispersion Based on Sulfonate and Monofunctional Polyethylene Oxide Polyether

Synthesis of hydroxy silane coupling agent and the silane-terminated polyurethane chain-extended by butanediol

Synthesis of Bis‐triethoxysilane Endcapped Polyurethane/urea and Its Self‐assembly Morphologies with the Assistance of Hydrogen Ion

Preparation of Polyurethane Ionomers by Reactive Extrusion and Dispersions Containing Sulfonate Groups and Polyethylene Glycol Segments

Synthesis and Characterization of High Solid Content Polyurethane Dispersion Containing Carboxylic and Sulfonic Groups

Synthesis of High-Solid Content Sulfonate-Type Polyurethane Dispersion by Pellet Process

Properties of high solid content polyurethane dispersion containing sulphonate and its films

Study on Synthesis and Performance of Sulfonated Waterborne Polyurethane

ONE-POT SYNTHESIS OF SULFONIC ACID GROUP-CONTAINING HYPERBRANCHED POLYURETHANE

The Synthesis of Ionic/Nonionic Complex Hydrophilic Monomer and the Investigation of Polyurethane Emulsions with Excellent Stability

Synthesis of Polyurethane-Acrylate Hybrid Emulsion Containing Siloxane and Fluorine

Synthesis and Properties of High Solid Content Sulphonated Waterborne Polyurethane Modified by HDI Trimer

Synthesis and characterization of sulfonate polyurea dispersions based on polyaspartic ester

Dynamic mechanical analysis of sulfonated polyurethane ionomers