Abstract:ABSTRACTA synthesis method of polyurethane ionomers (PUIs) and anionic/nonionic polyurethane dispersions (PUDs) is introduced in this article. PUIs were synthesized in twin‐screw extruder without organic solvent. PUIs were then dissolved in acetone and dispersed in water. The PUDs were obtained after distilling off acetone and the solid content of PUDs was about 55% and had excellent stability. PUDs obtained were mainly used as adhesives. PUIs were synthesized from poly(1,4‐butylene adipate glycol) (PBA) as soft segments, 1,4‐butanediol (BDO) and diphenylmethane diisocyanate‐50 (MDI‐50) as hard segments, poly(ethylene glycol) methyl ether (MPEG) and polyether diol‐containing sulfonate (SPPG) as hydrophilic monomers, and dibutyltin dilaurate (DBTDL) as catalyst. The particle size, viscosity, and adhesive properties of the PUDs were measured and the results indicated that PUDs obtained have excellent stability and adhesive properties, such as the maximum initial peel strength and T‐peel strength were 2.38 and 11.82 N mm−1, respectively. The thermal properties, tensile stress–strain, and water resistance of the PUIs films were also characterized. The test results showed that films have good thermal properties and water resistance properties, and some typical characteristics of crystalline polymers were revealed in the tensile stress–strain curves. © 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2019, 136, 47719.

Synthesis of High-Solid Content Sulfonate-Type Polyurethane Dispersion by Pellet Process

Synthesis and Characterization of Anionic/non-Ionic Type High Solid Content Polyurethane Dispersion Based on Sulfonate and Monofunctional Polyethylene Oxide Polyether

Synthesis and Characterization of High Solid Content Polyurethane Dispersion Containing Carboxylic and Sulfonic Groups

Preparation of Polyurethane Ionomers by Reactive Extrusion and Dispersions Containing Sulfonate Groups and Polyethylene Glycol Segments

Synthesis and Characterization of the High Solid Content Polyurethane Dispersion Which Made from the Polyester Polyol, Which Based on the Dimer Fatty Acid

High solid content polyurethane dispersion synthesized with polyester polyol based on dimer fatty acid

Synthesis of High Solid Content Polyurethane Dispersion Adhesive by Pellet Process

Synthesis and Characterization of the Anionic/Non-ionic and High Solid Content Polyurethane Dispersion with Different Soft Segments

Synthesis and Charactenization of High Solid Polyurethane Dispersion Based on Amino - sulfonate and TDI

Synthesis and characterization of polyurethane dispersions based on diaminocarboxylate

Synthesis and Characterization of High Solid Content Polycarbonate Diols Based Polyurethane Dispersions

Study on synthesis of PUD with different molecular weights and soft chain segments by pelleting process

Synthesis and characterization of high solid content aqueous polyurethane dispersion

Preparation and Characterization of UV Cured Polyurethane Dispersions with Sulfonate

Preparation and Characterization of Polyurethane Dispersions with MDI by Pelleting Process

Synthesis and characterization of sulfonate polyurea dispersions based on polyaspartic ester

Properties of high solid content polyurethane dispersion containing sulphonate and its films

High Biobased Carbon Content Polyurethane Dispersions Synthesized from Fatty Acid-Based Isocyanate

Synthesis and Properties of Anionic/Non-Ionic Aqueous Polyurethane Dispersion Modified with Polyaldehyde

Synthesis and Properties of High-Functionality Hydroxyl-Terminated Polyurethane Dispersions

High Solid Content Polyurethane Dispersions with Bimodal Particle Size Distribution